Hot Rolled 416 Stainless Steel Round Bar Solid Solution Stainless Steel Rod OD5 - 350mm
| Product Name | Stainless Steel Bar |
| Material | 201/202/301/304/304L/316/316L/309S/310S/321/409/410/416/420/430/2205/904L etc |
| Standard | ASTM,AISI,SUS,JIS,EN,DIN,BS,GB |
| Technique | Cold drawn/hot drawn/cold rolled/hot rolled |
| Surface | Pickled, bright, polished |
| Edge | Mill Edge, Slit Edge |
| Diameter | 8-130mm |
| Length | 5.8/6m or custom |
| Application | construction field, ships building industry, petroleum & chemical industries, military and electricity industries, food processing and medical industry, boiler heat exchange,machinery and hardware fields |
416 stainless steel round bar is a highly machinable grade 416 stainless steel, a martensitic chromium alloy. It has excellent strength and corrosion resistance properties and is commonly used for applications requiring high levels of machining accuracy, such as fasteners, bushings, and valve stems.
| Chemical Element | % Present |
|---|---|
| Carbon (C) | 0.06 - 0.15 |
| Chromium (Cr) | 12.00 - 14.00 |
| Manganese (Mn) | 0.0 - 1.50 |
| Silicon (Si) | 0.0 - 1.00 |
| Phosphorous (P) | 0.0 - 0.04 |
| Sulphur (S) | 0.15 - 0.35 |
| Molybdenum (Mo) | 0.0 - 0.60 |
| Iron (Fe) | Balance |
| Physical Property | Value |
|---|---|
| Density | 7.75 g/cm³ |
| Thermal Expansion | 9.9 x10^-6 /K |
| Modulus of Elasticity | 200 GPa |
| Thermal Conductivity | 24.9 W/m.K |
| Electrical Resistivity | 0.57 x10^-6 Ω .m |
| Mechanical Property | Value |
|---|---|
| Proof Stress | 450 Min MPa |
| Tensile Strength | 650 - 850 MPa |
416 stainless steel is martensitic stainless steel with high sulfur content. This sulfur content makes it more machinable, making it easier to turn, drill, and mill than stainless steel. This material also has excellent corrosion resistance and is a popular choice for applications that require a higher resistance to pitting and crevice corrosion. 416 stainless steel is relatively cheap and can be heat-treated to achieve different strength levels.
SS 416 bar offers great machinability, excellent corrosion and wear resistance, good formability, and improved strength over other traditional grades of stainless steel. It is ideal for use in highly corrosive environments requiring superior corrosion resistance, high-temperature applications, and those needing strength and ductility.
Machining 416 stainless steel round bars is relatively easy compared to other stainless steels. This material can be easily cut and shaped using standard machine tools. When machining, keeping the cutting tools sharp is recommended to avoid work hardening. 416 stainless steel has a lower ductility than austenitic stainless steel, which means it is more prone to breaking or chipping if not machined properly.
416 stainless steel round bars can be heat treated to achieve different strength levels. This process involves heating the material to a specific temperature and cooling it rapidly to achieve the desired properties. Heat treatment can improve the material’s machinability, toughness, and corrosion resistance. It is important to note that 416 stainless steel round bars should not be annealed as it can cause the material to lose its machinability.
Stainless steel 416 round bars can be welded using standard welding techniques such as TIG, MIG, and spot welding. However, it is important to note that this material is not recommended for welding as it can be prone to cracking. Welding should only be carried out by an experienced welder who has experience working with this material.