317L Stainless Steel Plate Thickness 3.0 - 30.0mm UNS S31703 / Alloy 317L Size 1.5*6m
Material | 200 300 400 Series stainless steel |
Grade | 201 202 301 303 304 304L 2205 2507 309 309S 310 310S 314 316L 316Ti
317L 321 2205 2507 409 409l 410 410S 420 420J1 420J2 430 441 444
904L |
Standard | AISI ASTM JIS DIN EN BS |
Tech | Cold rolled / Hot rolled |
Thickness | Hot rolled: 3mm-16mm 16-150mm Normal: 3.0 4.0 5.0 6.0 8.0 10.0 12.0 14.0 16.0 As per customer's request: 16-150mm Cold rolled: 0.3-6mm Normal:0.3/0.4/0.5/0.6/0.7/0.8/0.9/1.0/1.2/1.5/2.0/2.5/3.0 As per customer's request: 4.0/5.0/6.0 |
Width&Length | 1000mm-6000mm, or as per customer's request Hot rolled: 1250*3000mm (4.1*10ft) 1500*3000mm (5*10ft) 1250*6000mm (4.1*19.6ft) 1500*6000mm (5*19.6ft) 1800*6000mm (5.9*19.6ft) 2000*6000mm(6.5*19.6ft) Cold rolled: 1000*2000mm (3.2*6.5ft) 1219*2438mm (4*8ft) 1500*3000mm (5*10ft) 1800 available 2000 available |
Place of Origin | Jiangsu China |
Processing Service | Bending, Welding, Recoiling, Punching, Cutting |
Tolerance | ±1% |
Surface Treatment | N0.1,2B,BA,6K, 8K, 12k, N0.4, HL, Mirrored,checkered etc |
Payment | T/T terms, 30% pre-payment, 70% balance see B/L copy LC Western
Union Paypal |
Delivery Time | 5-15 days for ordinary orders (standard orders <=50 ton);
specified orders needs final confirmation as per customer's request |
317/317L is a molybdenum-bearing austenitic stainless steel with greatly increased resistance to chemical attack as compared to the conventional chromium-nickel austenitic stainless steels such as Alloy 304. In addition, Alloy 317L offers higher creep, stress-to-rupture, and tensile strength at elevated temperatures than conventional stainless steels. It is a low carbon or "L" grade which provides resistance to sensitization during welding and other thermal processes.
Alloy 317L is a lowcarbon corrosion resistant austenitic chromium-nickel-molybdenum stainless steel. The high levels of these elements assure the alloy has superior chloride pitting and general corrosion resistance to the conventional 304/304L and 316/316L grades. The alloy provides improved resistance relative to 316L in strongly corrosive environments containing sulfurous media, chlorides, and other halides.
The low carbon content of Alloy 317L enables it to be welded without intergranular corrosion resulting from chromium carbide precipitation enabling it to be used in the as-welded condition. With the addition of nitrogen as a strengthening agent, the alloy can be dual certified as Alloy 317.
Alloy 317L is non-magnetic in the annealed condition. It cannot be hardened by heat treatment, however the material will harden due to cold working. Alloy 317L can be easily welded and processed by standard shop fabrication practices.
If you are interested in other Stainless Steel Plates/Sheets, please click 302, 303, 304, 304L, 304H, 309, 309S, 310, 310S, 310H, 316, 316L, 317/317L, 317LMN, 321, 321H, 330, 347, 347H, 904L, 403, 405, 409, 410, 410S, 410/HT, 416, 416HT, 420, 422, 430, 440C, Duplex 2205, Duplex 2304, Duplex 2507.
| Carbon | Silicon | Sulfur | Phosphorus | Chromium | Molybdenum | Manganese | Nickel | Nitrogen |
| 0.030 | 0.75 | 0.030 | 0.045 | 18.0-20.0 | 3.0-4.0 | 2.00 | 11.0-15.0 | 0.10 |
| Yield Strengtd 0.2% Offset | Ultimate Tensile Strength | Elongation in 2 in. | Hardness | ||
| psi (min.) | (MPa) | psi (min.) | (MPa) | % (min.) | (max.) |
| 30,000 | 205 | 75,000 | 515 | 40 | 95 Rockwell B |
| Density lb/inᶟ | 0.285 |
| Density g/cmᶟ | 7.89 |
| Melting Range | 2540-2630°F/1390 – 1440 °C |
| Thermal Conductivity at 212°F (100°C) | 8.7 BTU/hr/ft²/ft/°F |
| Thermal Conductivity at 212°F (100°C) | 1.26 W/m-°K |
| Electrical Resistivity | 33.5 Microhm-in at 68°C |
| Electrical Resistivity | 85.1 Microhm-cm at 20°C |