ASTM B575 Hastelloy C276 Plate Sheet Nickel Alloy Plate Custom Laser Cutting Any Size
| Product Type | Hastelloy C276 ASTM B575 Sheet, Hastelloy C276 ASTM B575 Plate |
|---|---|
| Specification | ASTM B575 / ASME SB575 |
| Tolerances (width / thickness) |
|
| Dimensions |
|
| Thickness | 0.1 to 100 mm Thk |
| Width | 10-2500mm |
| Length | 2m, 2.44m, 3m, or as required |
| Finish | SATIN, 2B, 2D, BA NO (8), Cold rolled sheet (CR), Hot rolled plate (HR), No.1 finish hot rolled, 1D, No.4, BA, 8K, hairline, brush, mirror etc. |
| Hardness | Soft, Hard, Half Hard, Quarter Hard, Spring Hard |
| variety of shapes | Coils, Foils, Plates, Sheet, Strip, Plain Sheet, Checker Plates, Rolling Sheet, Flats, Clad Plates, Flat Sheet, Shim Sheet, Rolls, Blank (Circle), Rolling Plates, Flat Shim, soft annealed, descaled, tread Plates, sheared, annealed |
ASTM B575 UNS N10276 Hastelloy C276 Sheet is widely used in a variety of sectors, which include petrochemicals, chemical oil and gas, power production, pharmaceuticals, pulp and paper processing, and wastewater treatment. Hastelloy C276 Coil has a high tolerance to matching, stress degradation, and oxidising conditions. ASME SB 575 UNS N10276 content is often resistant to salt water corrosion in crevice environments, which may trigger aggressive assault in other products which are used on a large scale. UNS N10276 plate is normally remedy heat-treated at 2050 degrees Fahrenheit and easily quenched.
The materials used to make Hastelloy C-276 UNS N10276 Cold Rolled Plate must meet not only the chemical specifications, but also the mechanical requirements which have been stated in the ASTM B575 norm. When it comes to the mechanical properties of Hastelloy c276 Plate, this alloy must meet the requisite tensile properties. Various forms such as foils, sheets, strips, clad plate, coils, and other shapes and sizes.
| UNS N10276 Hastelloy C276 Plate melting range |
|---|
|
| ASTM B575 Alloy C276 Plate density |
|---|
|
| STANDARD | WERKSTOFF NR. | UNS | JIS | GOST | EN | OR |
| Hastelloy C276 | 2.4819 | N10276 | NW 0276 | ХН65МВУ | NiMo16Cr15W | ЭП760 |
| Grade | C | Mn | Si | S | Co | Ni | Cr | Fe | Mo | P |
| C276 | 0.010 max | 1.00 max | 0.08 max | 0.03 max | 2.50 max | 50.99 min* | 14.50 – 16.50 | 4.00 – 7.00 | 15.00 – 17.00 | 0.04 max |
| Element | Density | Melting Point | Tensile Strength | Yield Strength (0.2%Offset) | Elongation |
| Hastelloy C276 | 8.89 g/cm3 | 1370 °C (2500 °F) | Psi – 1,15,000 , MPa – 790 | Psi – 52,000 , MPa – 355 | 40 % |
| Material | Ultimate Tensile (min) | Yield Strength (Min) | Elongation % | Hardness Rb | ||
|---|---|---|---|---|---|---|
| Ksi | Mpa | Ksi | Mpa | |||
| C276 Plate | 107.4 | 741 | 50.3 | 347 | 67 | 89 |
| C276 Sheet | 115.5 | 796 | 54.6 | 376 | 60 | 86 |
C276 alloy Plate Metric Dimensions
| Plate Surface finish | Thickness (mm) | Width (max mm) |
|---|---|---|
| 2B – Cold rolled, heat treated, pickled, skin passed plate | 0.25–8.0 | 2032 |
| 2D – Cold rolled, heat treated, pickled plate | 0.4–6.35 | 1524 |
| 2E – Cold rolled, heat treated, mechanically descaled plate | 0.4–8.0 | 2032 |
| 2R – Cold rolled, bright annealed plate | 0.25–3.5 | 1524 |
| 2H – Work hardened plate | 0.4–6.35 | 1524 |
| Polished, brushed plate | 0.5–4.0 | 1524 |
Inconel
Inconel is a family of austenitic nickel-chromium-based superalloys.
Composition of Inconel
| Inconel | Element (% by mass) | ||||||||||||||
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
| Ni | Cr | Fe | Mo | Nb | Co | Mn | Cu | Al | Ti | Si | C | S | P | B | |
| 600 | 72.0 | 14.0–17.0 | 6.0–10.0 | 1.0 | 0.5 | 0.5 | 0.15 | 0.015 | |||||||
| 617 | 44.2–56.0 | 20.0–24.0 | 3.0 | 8.0–10.0 | 10.0–15.0 | 0.5 | 0.5 | 0.8–1.5 | 0.6 | 0.5 | 0.15 | 0.015 | 0.015 | 0.006 | |
| 601 | 58.0 | 20.0–23.0 | 5.0 | 8.0–10.0 | 3.15–4.15 | 1.0 | 0.5 | 0.4 | 0.4 | 0.5 | 0.1 | 0.015 | 0.015 | ||
| 690 | 59.5 | 30 | 9.2 | 0.35 | 0.01 | 0.02 | 0.35 | 0.019 | 0.003 | ||||||
| 718 | 50.0–55.0 | 17.0–21.0 | balance | 2.8–3.3 | 4.75–5.5 | 1.0 | 0.35 | 0.2–0.8 | 0.65–1.15 | 0.3 | 0.35 | 0.08 | 0.015 | 0.015 | 0.006 |
| X-750 | 70.0 | 14.0–17.0 | 5.0–9.0 | 0.7–1.2 | 1.0 | 1.0 | 0.5 | 0.4–1.0 | 2.25–2.75 | 0.5 | 0.08 | 0.01 | |||
Hastelloy
Hastelloy® could be a trademark for a series of high-strength, nickel based, corrosion resistant alloys created by Haynes Worldwide.
Hastelloy Melting Point, Density and Tensile Strength
| Density | Melting Point | Tensile Strength | Yield Strength (0.2%Offset) | Elongation | |
|---|---|---|---|---|---|
| C22 | 8.69 g/cm3 | 1399 °C (2550 °F) | Psi – 1,00,000 , MPa – 690 | Psi – 45000 , MPa – 310 | 45 % |
| C276 | 8.89 g/cm33 | 1370 °C (2500 °F) | Psi – 1,15,000 , MPa – 790 | Psi – 52,000 , MPa – 355 | 40% |
| B2 | 9.2 g/cm3 | 1370 °C (2550 °F) | Psi – 1,15,000 , MPa –760 | Psi – 52,000 , MPa – 350 | 40% |
| B3 | 9.2 g/cm3 | 1370 °C (2550 °F) | Psi – 1,15,000 , MPa –760 | Psi – 52,000 , MPa – 350 | 40% |
| C4 | 8.64 g/cm3 | 1350-1400 °C | 783 | 365 | 55% |
| Hybrid BC1 | 8.83 g/cm³ | 1343 - 1443°C | 725 | 310 | 40% |
| X | 8.22 g/cm³ | 1355°C | 655 MPa | 240 MPa | 35% |