| Product Name | 17-4PH Stainless Steel Foil |
| Grades | 17-4PH/630 |
| Hardness | 170HV-430HV or as customers’ requests |
| Thickness | 0.02mm-0.1mm |
| Width | 1.0mm-650mm |
| Edge | Slit/Mill |
| Quantity Tolerance | ±10% |
| Paper Core Internal Diameter | Ø500mm paper core, special internal diameter core and without paper core on customer request |
| Surface Finish | NO.1/2B/2D/BA/HL/Brushed/6K/8K Mirror,etc |
| Packaging | Wooden Pallet/Wooden Case |
| Payment Terms | 30% TT deposit and 70% balance before shipment, 100% LC at sight |
| Delivery Time | 5-7 working days |
| MOQ | 100Kgs |
| Shipping Port | Shanghai/Ningbo port |
| Sample | The sample is available |
17-4PH is a well-established precipitation hardening martensitic stainless steel capable of achieving very high strength and hardness after a relatively simple heat treatment. It offers excellent corrosion resistance combined with a structured range of mechanical property levels depending on the precise heat treatment applied.
The materials can be readily machined and fabricated in the softer tempers and can then be heat-treated to exceptional strength and dimensional stability. 17-4PH is widely used in the chemical, petrochemical, offshore, paper, and aerospace industries making best use of its outstanding corrosion resistance, wear resistance, strength and hardness.
Surgical and dental instrument, screwdriver.
17- 4 retains a high strength of precipitation hardening stainless steels a majority of applications are within the aerospace sector and OAG applications
The chemical components of grade 17-4PH stainless steel foil is summarized in the following table:
| C | Si | Mn | P | S | Cr | Ni | Cu | Nb |
| 0.07 max | 1.00 max | 1.00 max | 0.040 max | 0.030 max | 15.00~17.50 | 3.0~5.0 | 3.0~5.0 | 0.15~0.45 |
Alloy 17-4PH is provided in the solution-annealed condition (Condition A). Mechanical properties may be improved by subsequent age hardening treatments. These aging treatments are commonly described as conditions H900, H1025, H1075, H1150, H1150M and H1150D.
| Condition | UTS | 0.2% Yield | Elongation | Reduction of area | Hardness Brinel |
| H900 | 190.000 | 170.000 | 10 | 40 | 388 |
| H1025 | 155.000 | 145.000 | 12 | 45 | 331 |
| H1075 | 145.000 | 125.000 | 13 | 45 | 311 |
| H1150 | 135.000 | 105.000 | 16 | 50 | 277 |
| H1150m | 115.000 | 75.000 | 18 | 55 | 255 |
| H1150-D | 125.000 | 105.000 | 16 | 50 | 255 |