AISI 316 Iron Polished Stainless Steel Rod
301 is the steel that is most easily strengthened by cold deformation. Cold deformation can increase the strength and hardness of the steel, and retain sufficient plasticity and toughness. It has good rust resistance, but poor corrosion resistance, so it is not recommended for corrosive harsh environments. |
Specfications
| Commodity Description | |
| 1. Name of product | Stainless steel bar |
| 2. Diameter: | 3-300mm |
| 3. Shape: | Round, hexangular, square |
| 4. Standard: | ASTM, AISI, JIS, GB, DIN, etc. |
| 5. Material: | 201, 304, 304L, 316, 316L, 321, 309S, 310S, 904L |
| 6. Surface: | Bright, black |
| 7. Technique: | Cold/Hot Rolled |
| 8. Certification: | ISO |
| 9. Packing: | Standard export package or as your request |
| 10. Application: | Widely used in petroleum, Foodstuff, chemical industry, construction, electric power, nuclear energy, biotechnology, machinery, papermaking, etc. |
| 11. Advantages: | 1. Corrosion resistance. 2. High temprature resistance. 3. High production ability. 4. Reasonable price. 5. Excellent quality. 6. Various size. |
| 12. Main Market: | North America, South America, Europe, Southeast Asia, Africa, Oceania, Middle East, Eastern Asia, Central America |
| 13. MOQ; | 2 Metric Tons |
| 14. Delivery Time: | Within 7-30 working days |
| 15. Payment: | T/T, L/C, Western union |
Chemical Composition
| Specification | Grade | Chemical Composition(wt%) | ||||||
| C | Mn | Ni | Cr | Mo | Ti | |||
| ASTMJIS | 316L/022Cr17Ni12Mo2 | ≤0.03 | ≤2.0 | 10.0-14.0 | 16.0-18.0 | 2.0-3.0 | - | |
| JIS | SUS316L | ≤0.03 | ≤2.0 | 12.0-15.0 | 16.0-18.0 | 2.0-3.0 | - | |
| ASTMJIS | 316Ti/SUS 316Ti | ≤0.08 | ≤2.0 | 10.0-14.0 | 16.0-18.0 | 2.0-3.0 | 5*(C+N)-0.7 | |
Properties
| Spec | Grade | Mechanical Property | Physical Property | ||||
Y.S (N/MM2) | T.S (N/MM2) | EL (%) | HRB | Specific Heat (J/g℃) | Modulus of Elasticity (KN/mm2) | ||
| ASTM/GB | 316L/022Cr17Ni12Mo2 | ≥170 | ≥485 | ≥40 | ≤95 | 0.5 | 193 |
| JIS | SUS316L | ≥175 | ≥480 | ≥40 | ≤90 | 193 | |
| ASTM | 316Ti | ≥205 | ≥515 | ≥40 | ≤95 | 0.5 | 200 |
Applications:316L: Widely used in corrosion-susceptible environment and some mechanical components those are difficult to make heat treatment after forming in more corrosive environment.316Ti: Mainly used for industrial components. |