Baosteel Bright JIS 201 Stainless Steel Coil Master 85% Hardness

Item

  Stainless Steel 201 coil(Hot rolled, cold rolled)

Thickness

0.3~10.0mm

Width

1000mm, 1219mm, 1500mm, 1800mm, 2000mm, 2500mm, 3000mm, 3500mm, etc

Length

2000mm, 2440mm, 3000mm, 5800mm, 6000mm, etc

Standard

JIS, AISI, ASTM, GB, DIN, EN, etc

Surface

the surface and finish of stainless steel 201 coil:
2B, 2D, BA, NO.1, NO.4, NO.8, 8K, mirror, checkered, embossed, hair line, sand
blast, Brush, etching, etc

Brand:

Indian Origin, European Origin, Japanese Origin, US Origin, 

Korea Origin, Thailand Origin, Taiwan Origin

Manufacturer:

POSCO, Aperam, Jindal Stainless, DKC Korea, Thyssenkrup, 

Baosteel, TISCO, Arcelor Mittal, VDM, Nippon Metal, Outokumpu

Package

Shrink-wrapped ,Carton boxes,Wooden pallets,

Wooden boxes ,Wooden crates Etc.
required.

Export to

India, Indonesia, Malaysia, Singapore, Saudi Arabia, Qatar,

UAE, Iran, Iraq, Oman, South Africa, Nigeria, Kenya, Italy, 

UK, Brazil, Russia , Egypt , Kuwait , Taiwan, Australia .

STANDARD

WERKSTOFF NR.

UNS

JIS

AFNOR

BS

GOST

EN

SS 201

1.4372

S20100

SUS 201

-

-

-

-

Grade

C

Mn

Si

P

S

Cr

Mo

Ni

N

201

0.15 max

5.5-7.5

100 max

0.06 max

0.03 max

16.00-18.00

-

0.3-0.5

-

Properties

Metric

Imperial

Tensile strength (transverse at room temperature)

685 MPa

99400 psi

Tensile strength (longitudinal at room temperature)

696 MPa

101000 psi

Yield strength (transverse at room temperature)

292 MPa

42400 psi

Yield strength (longitudinal at room temperature)

201 MPa

43700 psi

Compressive yield strength

365 MPa

52900 psi

Elastic modulus

197 GPa

28573 ksi

Poisson’s ratio

0.27-0.30

0.27-0.30

Elongation at break (longitudinal at room temperature)

56%

56%

Elongation at break (transverse at room temperature)

62.50%

62.50%

Hardness, Rockwell B (transverse at room temperature)

85

85

Hardness, Rockwell B (longitudinal at room temperature)

85

85

Properties

Metric

Imperial

Density

7.86 g/cm3

0.284 lb/in³