3:1 Dual Wall Adhesive-Lined Heat-Shrink Polyolefin Tubing for Automotive and Marine Wire Harness
Product description: 3:1 Dual Wall Adhesive-Lined Heat-Shrink Polyolefin Tubing for Automotive and Marine Wire Harness
3:1 Dual Wall Adhesive-Lined Heat-Shrink Polyolefin Tubing for Automotive and Marine Wire Harness adopts flame retardant, cross-linked polyolefin with an inner coating of hot-melt adhesive and outer layer that shrinks to provide electrical and mechanical protection. The outer layer has excellent insulation, wear and corrosion resistant performances. Inner layer has the excellence of low melt point and waterproof etc. It has passed UL, RoHS, Reach certifications with 600V and 300V.
Application: 3:1 Dual Wall Adhesive-Lined Heat-Shrink Polyolefin Tubing for Automotive and Marine Wire Harness
3:1 Dual Wall Adhesive-Lined Heat-Shrink Polyolefin Tubing for Automotive and Marine Wire Harness with environmental sealing capability for a wide variety of electrical applications, including automotive and marine wire harness, wire spices, breakouts, and connector-to-cable transitions.
Dimension: 3:1 Dual Wall Adhesive-Lined Heat-Shrink Polyolefin Tubing for Automotive and Marine Wire Harness
| Inner Diameter | As Supplied(mm) ID | After Recovery(mm) | Standard Package (m/roll) | |||
| (mm) | (inch) | ID | Whole Wall Thickness | Adhesive Thickness | ||
| Φ2.4 | 3/32 | ≥2.4 | ≤0.80 | 0.85±0.15 | 0.40±0.10 | 200 |
| Φ3.2 | 1/8 | ≥3.2 | ≤1.00 | 0.95±0.15 | 0.40±0.10 | 200 |
| Φ4.8 | 3/16 | ≥4.8 | ≤1.60 | 1.10±0.15 | 0.40±0.10 | 100 |
| Φ6.4 | 1/4 | ≥6.4 | ≤2.20 | 1.20±0.15 | 0.45±0.10 | 100 |
| Φ7.9 | 5/16 | ≥7.9 | ≤2.70 | 1.35±0.15 | 0.50±0.10 | 100 |
| Φ9.5 | 3/8 | ≥9.5 | ≤3.20 | 1.45±0.20 | 0.50±0.15 | 50 |
| Φ12.7 | 1/2 | ≥12.7 | ≤4.20 | 1.70±0.20 | 0.50±0.15 | 1.22 |
| Φ15.0 | 5/8 | ≥15.0 | ≤5.20 | 1.80±0.20 | 0.55±0.15 | 1.22 |
| Φ19.1 | 3/4 | ≥19.1 | ≤6.30 | 2.00±0.20 | 0.55±0.15 | 1.22 |
| Φ25.4 | 1 | ≥25.4 | ≤8.50 | 2.10±0.25 | 0.55±0.15 | 1.22 |
| Φ30.0 | 1-1/4 | ≥30.0 | ≤10.20 | 2.20±0.25 | 0.60±0.15 | 1.22 |
| Φ39.0 | 1-1/2 | ≥39.0 | ≤13.50 | 2.40±0.25 | 0.60±0.15 | 1.22 |
| Φ50.0 | 2 | ≥50.0 | ≤17.00 | 2.70±0.25 | 0.80±0.15 | 1.22 |
| Φ64.0 | 2-1/2 | ≥64.0 | ≤21.00 | 3.00±0.30 | 0.80±0.20 | 1.22 |
| Φ76.0 | 3 | ≥76.0 | ≤25.00 | 3.00±0.30 | 1.00±0.20 | 1.22 |
| Φ90.0 | 3-1/2 | ≥90.0 | ≤30.00 | 3.00±0.30 | 1.00±0.20 | 1.22 |
| Φ100 | 4 | ≥100 | ≤34.00 | 3.00±0.30 | 1.00±0.20 | 1.22 |
| Φ125 | 5 | ≥125 | ≤42.00 | 3.00±0.30 | 1.00±0.15 | 1.22 |
Technical data: 3:1 Dual Wall Adhesive-Lined Heat-Shrink Polyolefin Tubing for Automotive and Marine Wire Harness
| Property | Test Method | Standard |
| Tensile Strength(MPa) | ASTM D2671 | ≥10.4 |
| Elongation | ASTM D2671 | ≥300 |
| Tensile Strength after Aging(MPa) | UL224 158℃*168hrs | ≥7.3 |
| Elongation after Aging(MPa) | UL224 158℃*168hrs | ≥200 |
| Dielectric Strength(KV/MM) | IEC243 | ≥15 |
| Volume Resistivity(Ω.cm) | ASTM D876 | ≥1*1014 |
Hot melt adhesive property: 3:1 Dual Wall Adhesive-Lined Heat-Shrink Polyolefin Tubing for Automotive and Marine Wire Harness
| Property | Test Method | Standard |
| Water Absorption | ASTM D570 | ≤0.2% |
| Softening Point | ASTM E8 | 95℃ |
| Strength of Pearing(PE) | ASTM D 1000 | 120N/25mm |
| Strength of Pearing(AL) | ASTM D 1000 | 80N/25mm |
Color: Standard color is black (other color available upon request).
Our services: 3:1 Dual Wall Adhesive-Lined Heat-Shrink Polyolefin Tubing for Automotive and Marine Wire Harness
3:1 Dual Wall Adhesive-Lined Heat-Shrink Polyolefin Tubing for Automotive and Marine Wire Harness