Sabic Lexan FXM163R resin is PC with Visual Effect, UV-Stabilizer, Heat Stabilized, Opaque. Colour package may affect properties. Application testing always recommended.
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, yield, 50 mm/min | 63 | MPa | ISO 527 |
| Tensile Stress, break, 50 mm/min | 70 | MPa | ISO 527 |
| Tensile Strain, yield, 50 mm/min | 6 | % | ISO 527 |
| Tensile Strain, break, 50 mm/min | 60 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 2350 | MPa | ISO 527 |
| Flexural Stress, yield, 2 mm/min | 90 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 2300 | MPa | ISO 178 |
| THERMAL | Value | Unit | Standard |
| CTE, 23°C to 80°C, flow | 7.E-05 | 1/°C | ISO 11359-2 |
| CTE, 23°C to 80°C, xflow | 7.32E-05 | 1/°C | ISO 11359-2 |
| Ball Pressure Test, 125°C +/- 2°C | PASSES | - | IEC 60695-10-2 |
| Vicat Softening Temp, Rate B/50 | 143 | °C | ISO 306 |
| Vicat Softening Temp, Rate B/120 | 145 | °C | ISO 306 |
| HDT/Ae, 1.8 MPa Edgew 120*10*4 sp=100mm | 127 | °C | ISO 75/Ae |
| PHYSICAL | Value | Unit | Standard |
| Mold Shrinkage on Tensile Bar, flow (2) | 0.5 - 0.7 | % | SABIC Method |
| Density | 1.2 | g/cm³ | ISO 1183 |
| Water Absorption, (23°C/sat) | 0.35 | % | ISO 62 |
| Moisture Absorption (23°C / 50% RH) | 0.15 | % | ISO 62 |
| Melt Volume Rate, MVR at 300°C/1.2 kg | 10 | cm³/10 min | ISO 1133 |
| Source GMD, last updated:03/02/2004 | |||
| Parameter | ||
| Injection Molding | Value | Unit |
| Drying Temperature | 120 | °C |
| Drying Time | 2 - 4 | hrs |
| Maximum Moisture Content | 0.02 | % |
| Melt Temperature | 280 - 310 | °C |
| Nozzle Temperature | 270 - 290 | °C |
| Front - Zone 3 Temperature | 280 - 310 | °C |
| Middle - Zone 2 Temperature | 270 - 290 | °C |
| Rear - Zone 1 Temperature | 260 - 280 | °C |
| Hopper Temperature | 60 - 80 | °C |
| Mold Temperature | 80 - 110 | °C |
| Source GMD, last updated:03/02/2004 | ||
For more information please download the datasheet | |