Sabic Valox 325Mresin is a high flow VALOX 325 for restrictive gate tooling (key buttons)
MECHANICAL | Value | Unit | Standard |
Tensile Stress, yld, Type I, 50 mm/min | 48 | MPa | ASTM D 638 |
Tensile Strain, brk, Type I, 50 mm/min | 180 | % | ASTM D 638 |
Flexural Stress, yld, 1.3 mm/min, 50 mm span | 81 | MPa | ASTM D 790 |
Flexural Modulus, 1.3 mm/min, 50 mm span | 2340 | MPa | ASTM D 790 |
Hardness, Rockwell R | 119 | - | ASTM D 785 |
IMPACT | Value | Unit | Standard |
Izod Impact, unnotched, 23°C | 1602 | J/m | ASTM D 4812 |
Izod Impact, notched, 23°C | 53 | J/m | ASTM D 256 |
Modified Gardner, 23°C | 40 | J | ASTM D 3029 |
THERMAL | Value | Unit | Standard |
HDT, 0.45 MPa, 6.4 mm, unannealed | 150 | °C | ASTM D 648 |
HDT, 1.82 MPa, 6.4 mm, unannealed | 55 | °C | ASTM D 648 |
Relative Temp Index, Elec | 120 | °C | UL 746B |
Relative Temp Index, Mech w/impact | 120 | °C | UL 746B |
Relative Temp Index, Mech w/o impact | 140 | °C | UL 746B |
PHYSICAL | Value | Unit | Standard |
Specific Gravity | 1.31 | - | ASTM D 792 |
Specific Volume | 0.76 | cm³/g | ASTM D 792 |
Water Absorption, 24 hours | 0.1 | % | ASTM D 570 |
Water Absorption, equilibrium, 23C | 0.34 | % | ASTM D 570 |
Mold Shrinkage, flow, 0.75-2.3 mm | 0.9 - 1.6 | % | SABIC Method |
Mold Shrinkage, flow, 2.3-4.6 mm | 1.5 - 2.3 | % | SABIC Method |
Mold Shrinkage, xflow, 0.75-2.3 mm | 1 - 1.7 | % | SABIC Method |
Mold Shrinkage, xflow, 2.3-4.6 mm | 1.6 - 2.4 | % | SABIC Method |
ELECTRICAL | Value | Unit | Standard |
Volume Resistivity | >2.2E+16 | Ohm-cm | ASTM D 257 |
Dielectric Strength, in air, 3.2 mm | 17.8 | kV/mm | ASTM D 149 |
Relative Permittivity, 100 Hz | 3.17 | - | ASTM D 150 |
Relative Permittivity, 1 MHz | 3.13 | - | ASTM D 150 |
Dissipation Factor, 100 Hz | 0.0014 | - | ASTM D 150 |
Dissipation Factor, 1 MHz | 0.0098 | - | ASTM D 150 |
Arc Resistance, Tungsten {PLC} | 4 | PLC Code | ASTM D 495 |
Hot Wire Ignition {PLC) | 3 | PLC Code | UL 746A |
High Voltage Arc Track Rate {PLC} | 1 | PLC Code | UL 746A |
High Ampere Arc Ign, surface {PLC} | 0 | PLC Code | UL 746A |
Comparative Tracking Index (UL) {PLC} | 0 | PLC Code | UL 746A |
FLAME CHARACTERISTICS | Value | Unit | Standard |
UL Recognized, 94HB Flame Class Rating (3) | 0.83 | mm | UL 94 |
CSA (See File for complete listing) | LS88480 | File No. | CSA LISTED |
UV-light, water exposure/immersion | F1 | - | UL 746C |
Source GMD, last updated:01/05/2000 |
Parameter | ||
Injection Molding | Value | Unit |
Drying Temperature | 120 | °C |
Drying Time | 3 - 4 | hrs |
Drying Time (Cumulative) | 12 | hrs |
Maximum Moisture Content | 0.02 | % |
Melt Temperature | 245 - 260 | °C |
Nozzle Temperature | 240 - 255 | °C |
Front - Zone 3 Temperature | 245 - 260 | °C |
Middle - Zone 2 Temperature | 240 - 255 | °C |
Rear - Zone 1 Temperature | 230 - 250 | °C |
Mold Temperature | 50 - 75 | °C |
Back Pressure | 0.3 - 0.7 | MPa |
Screw Speed | 50 - 100 | rpm |
Shot to Cylinder Size | 40 - 80 | % |
Vent Depth | 0.013 - 0.025 | mm |
Source GMD, last updated:01/05/2000 |
For more information please download the datasheet | |
Sabic Valox 325M.pdf |
Get The Latest Quotation
First-level distribution source in South China Reduce procurement costs, improve supply stability, Help you find the most suitable engineering plastic materials
Click to consult and get the latest quotation within 24 hours! |