ASME SA519 Seamless carbon steel and alloy steel mechanical tubes
Standard: ASTM A519 / ASME SA519
Steel grade: Carbon steel, alloy steel
Chemical composition:
| C, % | Mn, % | P, max, % | S, max, 5 | Si, % | Ni, % | Cr, % |
1010 | 0.08-0.13 | 0.3-0.6 | 0.04 | 0.05 | - | - | - |
1016 | 0.13-0.18 | 0.6-0.9 | 0.04 | 0.05 | - | - | - |
1020 | 0.18-0.23 | 0.3-0.6 | 0.04 | 0.05 | - | - | - |
1026 | 0.22-0.28 | 0.6-0.9 | 0.04 | 0.05 | - | - | - |
1035 | 0.32-0.38 | 0.6-0.9 | 0.04 | 0.05 | - | - | - |
1045 | 0.43-0.50 | 0.6-0.9 | 0.04 | 0.05 | - | - | - |
1541 | 0.36-0.44 | 1.35-1.65 | 0.04 | 0.05 | - | - | - |
4130 | 0.28-0.33 | 0.40-0.60 | 0.04 | 0.04 | 0.15-0.35 | - | 0.8-1.1 |
4135 | 0.33-0.38 | 0.7-0.9 | 0.04 | 0.04 | 0.15-0.35 | - | 0.8-1.1 |
4140 | 0.38-0.43 | 0.75-1.00 | 0.04 | 0.04 | 0.15-0.35 | - | 0.8-1.1 |
4145 | 0.43-0.48 | 0.75-1.00 | 0.04 | 0.04 | 0.15-0.35 | - | 0.8-1.1 |
4340 | 0.38-0.43 | 0.6-0.8 | 0.04 | 0.05 | 0.15-0.35 | 1.65-2.00 | 0.7-0.9 |
4130: Mo 0.15-0.25 4140: Mo 0.15-0.25 4145: Mo 0.15-0.25 4340: Mo 0.20-0.30 |
Process: cold drawn
Application: Tubes for machinery structure
Dimensional range:
OD: 19.05-76.2mm
Any specific size is to be discussed before offer
The tube be 100% eddy current tested
Ultrasonic test is as option
Straightness ≤1mm/1000mm
Roughness: Ra ≤0.8
Condition
Heat treatment
- A: Annealed
- N: Normalized
- QT: Quenched and tempered
- SR: Stress relieved or finish annealed
Coating
- When specified, tubing shall be coated with a film of oil before
shaping to retard rust. Should the order specify that tubing be
shipped without rust retarding oil, the film of oils incidental to
manufacture will remain on the surface. If the order specifies no
oil, the purchaser assumes responsibility for rust in transit.
- Unless otherwise specified, tubing may be coated with a rust
retarding oil on the outside and inside surfaces, at the option of
the manufacturer.
Test
- When specified, the hardness test shall be performed on 1% of the
tubes
- When the tension test is specified, one test will be performed on a
specimen from one tube per 2000 ft (610 m) or less for sizes over 3
in. (76.2 mm) and one tube per 5000 ft (1520 m) or less for sizes 3
in. (76.2 mm) and under.
- The yield strength corresponding to a permanent offset of 0.2 % of
the gage length of the specimen or to a total extension of 0.5 % of
the gage length under load shall be determined.
- Various types of nondestructive ultrasonic or electromagnetic tests
are available. The test to be used and the inspection limits shall
be established by manufacturer and purchaser agreement.
- When there are special requirements for steel cleanliness, the
methods of test and limits of acceptance shall be established by
manufacturer and purchaser agreement.
- When tubing suitable for flaring is required, the manufacturer
shall be consulted. When the grade and thermal treatment are
suitable for flaring, a section of tube approximately 4 in. (101.6
mm) in length shall stand being flared with a tool having a 60°
included angle until the tube at the mouth of the flare has been
expanded 15 % of the inside diameter without cracking or showing
flaws.
- When the flaring test is specified, tests shall be performed on two
specimens/5000 ft (1520 m) or less.