Excellent mechanical properties 95 / 5 HAA Polyester Resin good flow
Product Overview
From an application and performance standpoint, HAA has progressed
greatly, and to a large extent,
it is equal to or better than its TGIC counterpart. The primary
benefits HAA users see are enhanced
transfer efficiencies, better edge, and corner coverage. Companies
that apply HAA products see up
to 20% improvement in transfer efficiencies, more uniform film
builds across the part, and better
Faraday cage penetration. From a spray to waste standpoint, they
typically experience at least a 10%
reduction in over-all powder usage compared to a TGIC alternative.
Excessive film thickness > 5 mils
may have the potential for some out gassing (micro porosity) in the
cured film.
Product specifications
Excellent mechanical properties 95 / 5 HAA Polyester Resin good flow
| ||||||
| Code | Type | Acid Value mgKOH/g | Viscosity mPa.s/200℃ | T g ℃ | Curing ℃/min | Properties |
| YC7600B | 95:5 | 28-32 | 8000-10000 (220℃) | ≥62 | 180/10 | Excellent mechanical properties good flow |
Related Productions Display
| Code | Type | Acid Value mgKOH/g | Viscosity mPa.s/200℃ | T g ℃ | Curing ℃/min | Properties |
| YC8011 | 93:7 | 29-36 | 4000-6000 | ≥64 | 200/10 | Economical resin, excellent leveling and mechanical properties, good flexibility, |
| YC8012 | 93:7 | 29-34 | 5200-7200 | ≥63 | 200/10 | Economical resin,flow resistant, excellent mechanical properties |
| YC8016 | 93:7 | 29-36 | 4500-6500 | ≥64 | 200/10 | Economical resin,good leveling and mechanical properties |
| YC8200 | 93:7 | 29-34 | 4500-6500 | ≥62 | 200/10 | Excellent leveling, good mechanical properties and anti-aging performance; suitable for black high gloss,matt effect, slow curing |
| YC8211 | 93:7 | 28-36 | 3500-6000 | ≥65 | 200/10 | Excellent leveling and superior mechanical performance |
| YC8401 | 94:6 | 28-32 | 6000-8000 | ≥63 | 200/10 180/15 | Economical resin, excellent mechanical properties |
| YC8240 | 90:10 | 48-55 | 6000-9000 | ≥65 | 200/10 | High acid resin, high hardness, excellent comprehensive performance |
| YC8511 | 96:3 | 20-26 | 4500-5500 (220℃) | ≥65 | 200/10 | Excellent mechanical properties,suitable for home appliance |
| YC8600 | 93:7 | 30-36 | 6000-8000 | ≥65 | 200/10 | Excellent overall performance, widely used in aluminum profile |
| YC8666 | 93:7 | 33-38 | 6000-8000 | ≥67 | 200/10 | Excellent overall performance, widely used in aluminum profile, excellent resistance to water boiling and salt spray |
| YC8855 | 93:7 | 30-36 | 8000-10000 (220℃) | ≥70 | 200/10 | High temperature resistance(≤300℃), yellowing resistance, good leveling and mechanical properties, excellent weather resistance |
| YC8866 | 93:7 | 30-36 | 5500-7500 | ≥67 | 200/10 | High Tg,high gloss, good leveling, excellent weather resistance and storage stability |
| YC8868 | 93:7 | 30-38 | 5500-7500 | ≥69 | 200/10-15 | High Tg,high gloss, high leveling, excellent weather resistance and storage stability |
| YC8900 | 93:7 | 33-38 | 3500-5500 | ≥63 | 200/15 | Slow cure resin, excellent flow, for metal powder coating and architectural |
| For Heat Transfer Polyester Resin | ||||||
| Code | Type | Acid Value mgKOH/g | Viscosity mPa.s/200℃ | T g ℃ | Curing ℃/min | Properties |
| YC8205 | 92:8 | 38-44 | 3500-5000 | ≥63 | 200/10 | Excellent leveling, excellent mechanical properties and aging resistance, suitable for matt heat transfer |
| YC8206 | 92:8 | 40-45 | 4000-6000 | ≥69 | 200/10 | Good leveling, mechanical properties and weathering resistance, suitable for heat transfer |
| YC8208 | 93:7 | 37-40 | 7000-9000 | ≥68 | 200/10 | High gloss and hardness, excellent mechanical properties; suitable for heat transfer |
| Matt Dry Blend/One Shot System Standard Durable Polyester Resin | ||||||
| Code | Type | Acid Value mgKOH/g | Viscosity mPa.s/200℃ | T g ℃ | Curing ℃/min | Properties |
| YC8501 | 96:4 | 20-26 | 5000-9000 | ≥60 | 200/10 | Low acid resin for dry blend with 8502 to reach matt effect20-35%,used in matt weatherability powder coating |
| YC8502 | 90:10 | 48-53 | 4000-5500 | ≥67 | 200/10 | High acid resin, dry blend with 8501 to reach matt effect 20-35%, used in matt weatherability powder coating |
| TP009 | 93:7 | 30-36 | 4500-6500 | ≥60 | 220/15 | Good weather resistance and flexibility; can get dead matt effect with GMA |
| Superdurable Polyester Resin | ||||||
| Code | Type | Acid Value mgKOH/g | Viscosity mPa.s/200℃ | T g ℃ | Curing ℃/min | Properties |
| YC8588 | 93:7 | 29-34 | 4500-6500 | ≥64 | 200/15 | Super durable resin |
| YC8550 | 90/10 | 48-55 | 3500-7000 | ≥64 | 200/15 | Superdurable high acid resin, drying blend with YC8533 to reach matt |
| YC8533 | 93:7 | 30-35 | 2000-4000 | ≥62 | 200/15 | Superdurable, high flow, can dry blend with YC8550 to reach matt |
| YC8525 | 96:4 | 18-25 | 3000-5000 | ≥62 | 200/15 | Superdurable, high flow, can dry blend with YC8550 to reach matt |
| Low Temperature Curing Polyester Resin | ||||||
| Code | Type | Acid Value mgKOH/g | Viscosity mPa.s/200℃ | T g ℃ | Curing ℃/min | Properties |
| YC8700 | 93:7 | 30-36 | 4500-6500 | ≥60 | 160/15 | Low temperature fast curing resin, good leveling and mechanical properties |
| YC8718 | 93:7 | 30-36 | 3000-5000 | ≥60 | 160/15 | Low temperature fast curing resin, no blooming |