Quick Detail:
1. Injection Molding Grade
2.General Purpose
3. PA66+GF30%
Description:
PA66+GF30% LUMID GP2300B(W)Resin is designed for Injection Molding.
Applications:
Automotive Parts,Electric & Electronic Parts.
Datasheet:
| Properties | Test Condition | Test Method | Unit | Typical Value |
| Physical | ||||
| Specific Gravity | ASTM D792 | - | 1.37 | |
| Molding Shrinkage, 3.2mm | ASTM D955 | % | 0.4~0.9 | |
| Melt Flow Rate | ASTM D1238 | g/10min | ||
| Water Absorption | 23℃, 24hrs | ASTM D570 | % | 1.1 |
| Mechanical | ||||
| Tensile Strength, 3.2mm | ASTM D638 | |||
| @ Break | 5mm/min | kg/cm2 | 1,800 | |
| Tensile Elongation, 3.2mm | ASTM D638 | |||
| @ Break | 5mm/min | % | 2.9 | |
| Flexural Strength, 6.4mm | 3mm/min | ASTM D790 | kg/cm2 | 2,500 |
| Flexural Modulus, 6.4mm | 3mm/min | ASTM D790 | kg/cm2 | 87,500 |
| IZOD Impact Strength, 6.4mm | ASTM D256 | |||
| (Notched) | 23℃ | kg·cm/cm | 10 | |
| -30℃ | kg·cm/cm | |||
| Thermal | ||||
| Melting Temperature | ASTM D3418 | ℃ | 260 | |
| Heat Deflection Temperature, 6.4mm | ASTM D648 | |||
| (Unannealed) | 18.6kg | ℃ | 255 | |
| 4.6kg | ℃ | |||
| Coefficient of Linear Thermal Expansion | ASTM D696 | |||
| Flow | 10-5 m/m℃ | 3 | ||
| Cross-flow | 10-5 m/m℃ | |||
| Ball Pressure Temperature | IEC 60695-10-2 | ℃ | ||
| Burning Rate, 3.2mm | FMVSS 302 | mm | ||
| Flammability | UL94 | |||
| 0.75mm | class | HB | ||
| 1.5mm | class | HB | ||
| 3.0mm | class | HB | ||
| Relative Temperature Index | UL 746B | |||
| Electrical | 120 | ℃ | ||
| Mechanical with Impact | 110 | ℃ | ||
| Mechanical without Impact | 120 | ℃ | ||