ABS BM662B Blow Molding Grade Plastic Raw Material with Heat Resistance for Automotives Exterior Housing(Spoiler, Bumper Guard.)
ABS BM662B Quick Detail:
1. Blow Molding
2. Heat Resistance
ABS Plastic Raw Material Description:
1. Blow Molding ABS grade
2. Heat Resistance: Higher HDT with 97℃.
ABS BM662B Applications:
Automotives Exterior Housing(Spoiler, Bumper Guard.)
ABS BM662B Datasheet:
| Properties | Method | Unit | BM662B |
| Physical | |||
| Specific Gravity , 23℃ | ASTM D792 | 1.05 | |
| Mold Shrinkage , 23℃, 3.2mm , 23℃ | ASTM D955 | % | 0.4 ~ 0.7 |
| Melt Flow Rate , 220℃, 10kg | ASTM D1238 | g/10min | 2 |
| Mechanical | |||
| Tensile Strength at Yield , 23℃, 50mm/min, 3.2mm | ASTM D638 | Mpa | 46 |
| Tensile Elongation at Break , 23℃, 50mm/min, 3.2mm | ASTM D638 | %, (Min) | 10 |
| Tensile Modulus , 23℃, 50mm/min, 3.2mm | ASTM D638 | MPa | 1900 |
| Flexural Strength , 23℃, 15mm/min, 3.2mm | ASTM D790 | Mpa | 70 |
| Flexural Modulus , 23℃, 15mm/min, 3.2mm | ASTM D790 | MPa | 2050 |
| Izod Impact Strength , Notched, 3.2mm, 23℃ | ASTM D256 | J/m | 160 |
| Izod Impact Strength , Notched, 3.2mm, -30℃ | ASTM D256 | J/m | 70 |
| Izod Impact Strength , Notched, 6.4mm, 23℃ | ASTM D256 | J/m | 160 |
| Izod Impact Strength , Notched, 6.4mm, -30℃ | ASTM D256 | J/m | 60 |
| Rockwell Hardness , R-Scale | ASTM D785 | 100 | |
| Thermal | |||
| HDT , Edgewise, 1.82MPa, 6.4mm, Unannealed | ASTM D648 | ℃ | 103 |
| VICAT , 50N, 50℃/h | ASTM D1525 | ℃ | 110 |
ABS BM662B Caution:
1. PLEASE REFER TO THE MATERIAL SAFETY DATA SHEET (MSDS) FOR MORE DETAILS.
2. SOME PHISICAL AND/OR CHEMICAL PROPERTIES OF THIS PRODUCT MAY CHANGE WHEN IT'S MIXED WITH OTHER CHEMICAL PRODUCTS. PLEASE TEST IT AND CONFIRM BEFORE USING IT IN THE CONDITION ABOVE.
3. CARE SHOULD BE TAKEN TO AVOID ACCIDENTS WHEN LOADING, UNLOADING OR STACKING THE PRODUCT.
Caution:
1. AVOID DIRECT SUNLIGHT, STORE IN COOL, DRY VENTILATED AREA.
2.KEEP AWAY FROM THE HEAT, SPARK, AND FLAME.
3. DO NOT INHALE GASEMITTED FROM THE HEATED RESIN.
4. DIRECT CONTACT WITH THE MELTED RESIN MAY CAUSE SEVERE BURNS.
5. THE WORKSHOP FLOOR SHOULD BE KEPT CLEAN AT ALL TIMES IN ORDER TO PREVENT ACCIDENT ASSOCIATED WITH LOOSE PELLETS OR FILM
6. DO NOT EAT THE PELLETS AND AVOID INHALING DUST PARTICLES IN THE PACKAGING BAGS.
7. ENSURE THE PELLETS AND PACKAGING BAGS ARE DISPOSED OF PROPERLY AND IN COMPLIANCE WITH LOCAL/STATE REGULATION.
8.LIFTING OF HEAVY BAGS CAN CAUSE DAMAGE TO YOUR SPINE IF NOT DONE CORRECTLY
9. CARE SHOULD BE TAKEN TO AVOID ACCIDENTS WHEN LOADING, UNLOADING OR STACKING THE PRODUCT.
10. THIS BAG SHOULD NOT BE USED FOR ANY OTHER PURPOSES EXCEPT FOR PACKING THE PELLETS.
11. PLEASE REFER TO THE MATERIAL SAFETY DATA SHEET (MSDS) FOR MORE DETAILS.
12. SOME PHISICAL AND/OR CHEMICAL PROPERTIES OF THIS PRODUCT MAY CHANGE WHEN IT'S MIXED WITH OTHER CHEMICAL PRODUCTS. PLEASE TEST IT AND CONFIRM BEFORE USING IT IN THE CONDITION ABOVE.