Properties | Method | Unit | HF380I |
Physical | | | |
Specific Gravity , 23℃ | ASTM D792 | | 1.04 |
Mold Shrinkage , 23℃, 3.2mm , 23℃ | ASTM D955 | % | 0.4 ~ 0.7 |
Melt Flow Rate , 220℃, 10kg | ASTM D1238 | g/10min | 38 |
Mechanical | | | |
Tensile Strength at Yield , 23℃, 50mm/min, 3.2mm | ASTM D638 | Mpa | 43 |
Tensile Elongation at Yield , 23℃, 50mm/min, 3.2mm | ASTM D638 | %, (Min) | 5 |
Tensile Elongation at Break , 23℃, 50mm/min, 3.2mm | ASTM D638 | %, (Min) | 10 |
Tensile Modulus , 23℃, 50mm/min, 3.2mm | ASTM D638 | MPa | 2100 |
Flexural Strength , 23℃, 15mm/min, 3.2mm | ASTM D790 | Mpa | 70 |
Flexural Modulus , 23℃, 15mm/min, 3.2mm | ASTM D790 | MPa | 2400 |
Izod Impact Strength , Notched, 3.2mm, 23℃ | ASTM D256 | J/m | 270 |
Izod Impact Strength , Notched, 3.2mm, -30℃ | ASTM D256 | J/m | 110 |
Izod Impact Strength , Notched, 6.4mm, 23℃ | ASTM D256 | J/m | 270 |
Izod Impact Strength , Notched, 6.4mm, -30℃ | ASTM D256 | J/m | 110 |
Rockwell Hardness , R-Scale | ASTM D785 | | 106 |
Thermal | | | |
HDT , Edgewise, 1.82MPa, 6.4mm, Unannealed | ASTM D648 | ℃ | 85 |
VICAT , 50N, 50℃/h | ASTM D1525 | ℃ | 93 |
RTI Electrical | UL 746B | ℃ | 60 |
RTI Mechanical with Impact | UL 746B | ℃ | 60 |
RTI Mechanical without Impact | UL 746B | ℃ | 60 |
Flammability, 1.5mm | UL 94 | | HB |
Flammability, 3.0mm | UL 94 | | HB |