PVDF / Ptfe Sleeve Bearing , Anti - Corrosion Plastic Ball Bearings

Country/Region	china
City & Province	jiaxing zhejiang
Categories	Seals

Product Details

PVDF/PTFE Anti-corrosion Plastic Bearings

As the typical type of fluoroplastic, PTFE and PVDF have the most excellent anti-corrosion performance, Among them PTFE has the best anti-corrosion performance of all the engineering-plastics known to man, PVDF/PTFE Anti-corrosion Plastic Bearings could be used in all the Strong Acid and Alkali application, including HF and smoke formation H2SO4 HNO3 or HCL (98% above) etc., and PVDF/PTFE Anti-corrosion Plastic Bearings could be used in high temperature application. PTFE could be used in 180℃ and PVDF in 150℃. But PTFE has very low mechanical strength, easy to be out of shape and have large Dimension change when the temperature rise or reduce.

The Density of PVDF plastic bearings is 1.77 g/cm3, PTFE plastic bearings is 2.18 g/cm3, Sliding friction coefficient is 0.30 and 0.10, Short-time highest application temperature is 150℃ and 260℃.

So PVDF/PTFE Anti-corrosion Plastic Bearings couldn't be used in heavy load and high-speed occasion. Compared with PTFE, PVDF has better comprehensive performance. Generally the rings and cage were made with PTFE or PVDF, Balls were made with glass, ceramic or stainless.

Basic properties of staple engineer plastic
Material	HDPE	PP	POM	PA66	PVDF	PPS	PTFE	PEEK
Long-time working temp.	90	100	110	100	150	230	260	280
Density	g/cm3	0.91	1.42	1.14	1.77	1.35	2.18	1.32
Ball indentation hardness	50	80	170	170	80	190	30
Tensile stress	25	30	70	80	50	75	25	95
Sliding friction coefficient	0.29	0.3	0.34	0.35-0.42	0.3		0.08-0.1	0.3-0.38
Melted temperature	130	165	175	260	172	280	327	343
Short-time highest application temperature	90	140	150	170	150	260	260	300
Coet of Inear expansion (10^-5/K)	13-15	17	10	8	13	5	12	5
Dielectric constant at 1 Mhz(10^6HZ)	2.4	2.25	3.7	3.6-5	8		2.1	3.2-3.3
Volume resisrivity (Ω·cm)	>10^15	>10^24	>10^14	10^13	10^12	>10^13	10^14	10^13
flammability UL94	+	+	-	(+)	(+)	-	+	+
Anti-weathering	-	-	-	-	-	-	+	-
Note: + =resistant; (+) =partly resistant; - =non-resistant

Chemical properties of Engineer plastic
Chemical Composition	Material
Chemical Composition	PI	PEEK	PTFE	PVDF	PA66	POM	PP	HDPE	ABS
Acrtate	+	+	+	(+)	(+)	+	+	(+)	+
Formic acid (10% water)	+	+	+	+	-	-	+	+	+
Ammonia (10% water)	-	+	+	+	+	(+)	+	+	+
Aether	+		+	+	+	+	+	+
Petrol	+	+	+	+	+	+	(+)	(+)	(+)
Bori acid (10% water)		+	+	(+)	+	+	+	+	+
Aminoform	+	+	+		-	-	(+)	-	-
Aeti aid 100%	(+)	-	+		-	-	+	+	-
Aceti aid (10% water)	+	+	+		-	(+)	+	+	+
HF			+		-	-	+	+	(+)
Formaldehyde aqu (30% water)		+	+	+	+	-	+	+	+
Glycerin	+		+		+	+	+	+	+
Iodine, Glycol	+		+	(+)	-	(+)	+	+	(+)
K2Cr2O7 (10% water)			+	+	+	-	+	+	+
KMnO4 (1% water)	+	+	+	+	-	(+)	+	+	(+)
2-Hydronyprpionic 10%	+		+	+	-	-	+	+	-
2-Hydronyprpionic 90%	+	+	+	+	+	(+)	+	+	+
Nad (10% water)	+	+	+	+	+	+	+	+	+
NaNO3 (10% water)	+		+	+	+	+	+	+	+
NaOH (50% water)		+	+	+	+	-	+	+	+
NaOH (5% water)			+	+	+	-	+	+
Oxalic (10% water)	+	+	+	+	(+)	(+)	+	+	+
Tetracarp	+		+	+	(+)	+	-	-	(+)
H3PO3 100%		+	+		-			+	+
H3PO4 (10% water)		+	+	+	-	-	+		+
NHO3 (2% water)	+	+	+	+	-	-	+	+	+
HCL (2% water)	+	+	+	(+)	-	-	+	+	+
H2SO4 98%		-	+		-	-	+	(+)	-
Soap liquid			+	+	+	+	+	+
Alkaliliquid (10% water)			+	+	+	+	+	+	+
Toluene	+	+	+	+	+	+	+	(+)	-
Water, cold	+	+	+	+	+	+	+	+	+
Water, hot		+	+	+	(+)	-	+	+	+
H2O2 (30% water)		(+)	+	+	-	-	+	+	+
H2O2 (0.5% water)	+		+	+	-	(+)	+	+	+
Asphalt	+		+		(+)	+	(+)	(+)
Note: + =resistant; (+) =partly resistant; - =non-resistant