Polyaspartic Wear Resistance self-leveling Flooring Coating PF864

Polyaspartic Flooring Coating PF864

1. PRODUCT NAME  PF864  Polyaspartic Flooring Topcoat

2. PRODUCT DESCRIPTION

PF864 Polyaspartic Flooring Topcoat  is a super abrasion resistant fast-curing three-part polyaspartic aliphatic polyurea sealer/finish coating for industrial applications. The material is applied in single or multiple coats by brush, roller or squeegee varying thicknesses to a variety of substrates including concrete and metal. It can be applied as a top coat employed within seamless multi-buildchip/quartz seamless flooring systems. The important characteristics of PF864 are its rapid-cure capabilities, high bond strength and UV resistance.

PF864 provides optimal impact, abrasion, and chemical resistance characteristics. Suitable for high traffic applications. The material is ideal for use as a primer, intermediary coating, or clear topcoat sealer within interior resinous flooring applications requiring minimal installation odor.

3. TECHNICAL DATA

4. INSTALLATION

Surface Preparation

Surfaces to be coated must be free of grease and any other contaminants that may impede adhesion. Always check the surface for any bond inhibitors prior to application. Any repairs must be addressed prior to application and should be repaired in accordance with ICRI standards. A moisture emission measurement system is necessary to assess the moisture drive of a concrete slab prior to installation of any toppings or coatings. The transmission rate must not exceed three pounds per 1,000 square feet per 24 hours. The relative humidity of the slab must not exceed 75% as tested per ASTM F2170 Relative Humidity in Concrete Slab test. If there is a moisture emission situation in excess of the above rate, use Moisture Vapor Barrier. The application process will depend on the system being installed, reference appropriate specification for details.

PF864 may be used as a top-coat or applied direct to concrete. Concrete must be ground to an ICRI CSP-2 profile or the equivalent of 30-60-grit sandpaper. This profile is achieved with a surface grinder

equipped with metal bond diamonds.

Mixing

Maintaining a consistent storage temperature prior to application will maximize working time.

Mixing Part A with Part B

Mix part A and part B in equal parts (1:1) using a clean, dry working vessel. Use a paddle mixer on slow speed for 2 minutes. Avoid over-mixing or creating a vortex that would introduce air. Do not mix below the dew point, which will shorten the pot life. No induction time is required prior to use. If micro-media agents are to be incorporated, they are to be added after thoroughly mixing A and B.

5. ADVANTAGE

Part A: 20kgs pail

Part B: 20kgs pail

n Shelf Life

12 months unopened. Store at 40°F to 75°F (4°-24°C) in a covered area (out of the sun). Material should be kept in a cool dry place prior to application.

n Color

PF864 is transparent clear coat reference appropriate specification for details.

PF864 may be used as a top-coat or applied direct to concrete. Concrete must be ground to an ICRI CSP-2 profile or the equivalent of 30-60-grit sandpaper. This profile is achieved with a surface grinder equipped with metal bond diamonds.

You may want to know more about how to with us, click here.

Changsha Perflex Novel Materials Corp.,Ltd

Mail: sales@perflex.com.cn | Tel/Whatsapp:+ 0086 183 9099 2093

Web: www.tile-sealant.com | www.tile-sealer.com

Add: Baofeng Industrial Zone, Shashi County, Liuyang, Changsha City, Hunan China