96% 1mm white high Temperature Resistance thickness high alumina
ceramic plate
Advantages
Alumina ceramics are the most versatile of the advanced technical
ceramics stronger than the traditional ceramics chemically inert -
excellent corrosion resistance
outstanding electrical insulators, even at very high temperatures
extremely hard - excellent abrasion resistance are almost unaltered
at 1000°C useable up to 1700°
All alumina bodies possess very good mechanical properties such as
hardness and compressive strength. They also hold up well under
harsh conditions such as acid corrosion, high wear areas, and
sliding abrasion. They also possess very good electrical insulation
properties and have very specific thermal conductive and thermal
expansion rates.
Product Description
Mullite is a rare silicate mineral of post-clay genesis, It is
produced during various melting and firing processes. Corundum
mullite crucibles with high temperature resistance has the
characteristics of compact structure, high compressive strength,
good thermal shock stability, acid and alkali corrosion resistance,
anti stripping, anti pulverization and long service life. The
products are widely used in the smelting of rare earth magnetic
materials, alloy materials and sintering of ceramic powders.
| Feature | Ceramic Parts |
| Color | White |
| Material | Alumina ceramic |
| Size | Customized |
| Brand Name | Feifan ceramic |
| Certification | ISO9001, SGS, ROHS |
| Used | Industry |
Corundum mullite material performance table | ||||
| Chemical components | Al2O3 | 90﹪ | ||
| SiO2 | 9% | |||
| TiO2 | 1% | |||
| Fe2O3 | ||||
| CaO/MgO | ||||
| K2O/Na2O | ||||
| Density | g/cm3 | 2.73 | ||
Physical characteristics | Water absorption | ％ | 15% | |
| Sintering temperature | ℃ | 1650 | ||
| Hardness | HV | 1000 | ||
| Flexural strength | Mpa | 9.3 | ||
| Compressive strength | Mpa | 50 | ||
| Fracture toughness | Map.m3/2 | - | ||
| Maximum use temperature | ℃ | 1700 | ||
Thermal characteristics | Thermal expansion coefficient | /℃ | 6*10-6 | |
| Thermal shock resistance | T(℃) | 300 | ||
| Thermal conductivity | W/m.k(25-300℃) | 4.2 - | ||
Electrical performance | 20℃ | >1012 | ||
| Volume resistivity | 100℃ |
>.cm | 1010-1012 | |
| 300℃ | - | |||
| Insulation breaking strength | KV/mm | 10 | ||
| Dielectric constant | 100MHz(E) | 6 | ||
About us
1. We are one of the leading manufacturer specialized in designing
and manufacturing industrial ceramics with experience of more than
10 years in China
2. Manufacturing according to the ISO9001:2008 quality control
system guidelines.
3. Our products are widely recognized and trusted by users and can
meet continuously developing economic and social needs.
4. Workers are locals in china, low production cost.