Density 8.4 g/cm³
Melting Range
1315-1350°C
Casting Temperature 1500°C
Preheating Temperature of Mould 900-950°C
Coefficient of expansion 20-600°C
CTE 14.1 μm/mK
Vickers Hardness 194 HV10
Elongation at rupture 16%
Tensile Strength 546 N/mm2
Yield Strength 309 N/mm2
E-Modulus 172.000 N/mm2
Chemical Compound
Ni 62%, Cr 24.50%, Mo 11%, Si 1.7%, Fe 0.5%, Traces: Co, C