Heat Resistance Magnesia Carbon Brick For Refractory Material
Magnesia Carbon Bricks Product description:
Magnesia Carbon brick is resin-bonded brick made from dead-burned or fused magnesia and graphite. Anti-oxidant is added if required. Magnesia Carbon brick has good performance in thermal resistance, corrosion resistance and spalling resistance. Widely used in converters, EAFs, ladles and refining furnaces.
1.Phosphoric acid reactor.
2.Phosphoric acid scrubber lining.
3.Phosphoric and hydrochloric acid, hydrofluoric acid storage tank lining.
4.Power plant to remove sulfur tower and chimney lining.
Magnesia Carbon Bricks Physical and chemical indicators:
牌号 Brand | XY-MT8A | XY-MT8B | XY-MT8C | XY-MT10A | XY-MT10B | XY-MT10C | XY-MT12A | XY-MT12B | XY-MT14A | XY-MT14B |
| MgO | 82 | 82 | 78 | 80 | 78 | 76 | 78 | 76 | 78 | 76 |
| C | 8 | 8 | 8 | 10 | 10 | 10 | 12 | 12 | 14 | 14 |
显气孔率/ %,≤ Apparent porosity | 5 | 6 | 7 | 4 | 5 | 6 | 4 | 5 | 4 | 5 |
体积密度/ g﹒cm-3,≥ Bulk density | 3.0 | 2.95 | 2.95 | 3.0 | 2.95 | 2.95 | 2.98 | 2.96 | 2.98 | 2.96 |
耐压强度/ MPa,≥ Crushing strength | 45 | 40 | 35 | 40 | 40 | 35 | 40 | 40 | 40 | 40 |
高温抗折强度(1450℃)/ MPa,≥ Hot modulus of rupture | 6 | 5 | 4 | 8 | 7 | 6 | 8 | 7 | 12 | 10 |
牌号 Brand | XY-MT12A | XY-MT12B | XY-MT12C | XY-MT14A | XY-MT14B | XY-MT14C | |
化学成分/ %,≥ Chemical composition | MgO | 78 | 76 | 74 | 78 | 76 | 74 |
| C | 12 | 12 | 12 | 14 | 14 | 14 | |
显气孔率/ %,≤ Apparent porosity | 4 | 5 | 6 | 4 | 5 | 6 | |
体积密度/ g﹒cm-3,≥ Bulk density | 2.98 | 2.96 | 2.95 | 2.98 | 2.96 | 2.95 | |
耐压强度/ MPa ,≥ Crushing strength | 40 | 40 | 35 | 40 | 40 | 35 | |
高温抗折强度(1450℃)/ MPa,≥ Hot modulus of rupture | 8 | 7 | 6 | 12 | 10 | 8 | |
Specifications of Magnesia Carbon Brick
Magnesia Carbon Bricks Advantage
Magnesia Carbon Brick has excellent corrosion resistance together with good thermal shock properties.
MgO-C bricks offers good oxidation resistance due to use of high purity flake graphite.