CNC Machined W90Cu10 Tungsten Copper Alloy Spare Parts
Tungsten Copper alloy Properties:
Tungsten-copper alloy features good heat and electrical conductive, high temperature resistance strength and ductility.
Tungsten copper alloy applications:
Tungsten copper alloy has wide applications. Tungsten copper alloy
is widely used to manufacture switch contact for high-voltage
electrical appliances, rocket nozzle throat liner and sternpost
rudder, and other high temperature components and parts. In
addition, it also can be used to make electrode for spark processing, high temperature mold and other high heat and electrical
conductive parts. And also WCu alloy can be applied as electrodes
for electrical machining.
Tungsten Copper Alloy types,chemical compositions and main properties:
| Type | chemical composition of copper tungsten alloy(%) | resistivity(cm) | tensile strength(kg/mm2) | hardness | density(g/cm3) | |
| W | Cu | |||||
| F6002E | 60 | balance | <=3.26*10-6 | >=130 | >=160 | >=12.70 |
| 70 | <=3.80*10-6 | >=200 | >=13.80 | |||
| 80 | <=4.00*10-6 | >=220 | >=15.00 | |||
| Brand and NO. | Chemical components% | Physical properties | ||||||
Cu | Total impurities ≤ |
W | Density (g/cm³) ≥ | Hardness HB ≥ | Resistivity (µΩ·cm) ≤ | Conductivity IACS%≥ | Bending strength Mpa≥ | |
| CuW(50) | 50±2.0 | 0.5 | Bal. | 11.85 | 115 | 3.2 | 54 | |
| CuW(55) | 45±2.0 | 0.5 | Bal. | 12.30 | 125 | 3.5 | 49 | |
| CuW(60) | 40±2.0 | 0.5 | Bal. | 12.75 | 140 | 3.7 | 47 | |
| CuW(65) | 35±2.0 | 0.5 | Bal. | 13.30 | 155 | 3.9 | 44 | |
| CuW(70) | 30±2.0 | 0.5 | Bal. | 13.80 | 175 | 4.1 | 42 | 790 |
| CuW(75) | 25±2.0 | 0.5 | Bal. | 14.50 | 195 | 4.5 | 38 | 885 |
| CuW(80) | 20±2.0 | 0.5 | Bal. | 15.15 | 220 | 5.0 | 34 | 980 |
| CuW(85) | 15±2.0 | 0.5 | Bal. | 15.90 | 240 | 5.7 | 30 | 1080 |
| CuW(90) | 10±2.0 | 0.5 | Bal. | 16.75 | 260 | 6.5 | 27 | 1160 |