LT·E711 AWS E71T-1C Flux Cored Arc Welding Wire
LT·E711 1.2/1.4/1.6mm CO2 Gas Shielded Flux Cored Arc Welding Wire
E71T-1C was developed for welding mild steel and 490MPa high
tensile strength steel and launched into the world of arc welding
nearly 30 years ago.
The prefix of the trade designation, DW, was coined from the words,
Dual Wire, because the wire consists of steel sheath and cored
flux. This development provided the momentum for shipbuilders and
bridge constructors in particular to employ semiautomatic and
automatic welding with
E71T-1C instead of shielded metal arc welding with covered
electrodes. This is why E71T-1C is called an epoch-making
flux-cored wire.
LT·E711 Conform to Standard :
GB/T 10045 E501T-1
AWS A5.36 E71T-1C
JIS Z3313 E492T1-1CA
ISO 17632-B-T492T1-1CA
Purpose:Most widely used for welding some key structures like shipbuilding, mechanical manufacture, pressure vessels, boilers, petroleum machinery, chemical machinery, hoisting machinery
Chemical Composition(%)(Shielding Gas:CO2)
| Chemical Composition | C | Mn | Si | S | P |
| Guarantee Value | ≤0.18 | ≤1.75 | ≤0.90 | ≤0.030 | ≤0.030 |
| General Result | 0.05 | 1.28 | 0.39 | 0.010 | 0.016 |
Mechanical Properties of Deposited Metal(Shielding Gas:CO2)
| Test Item | Rm(MPa) | ReL/Rp0.2(MPa) | A(%) | KV2(J) |
| -20℃ | ||||
| Guarantee Value | ≥480 | ≥400 | ≥22 | ≥27 |
| General Result | 550 | 470 | 27 | 115 |
Diffusion hydrogen content of the deposited metal (Mercury Method):≤10ml/100g
X-Ray Radiographic Test Requirements:Grade II
Reference Current(DC+)
| Size(mm) | Φ1.2 | Φ1.4 | Φ1.6 | |
| Current Range (A) | Flat Position | 120~300 | 150~400 | 180~450 |
| Vertical Upward welding/ Overhead position | 120~260 | 150~270 | 180~280 | |
| Vertical Downward weldingOverhead position | 200~300 | 220~300 | 250~300 | |
| Horizontal Welding | 120~280 | 150~320 | 180~350 | |
Notes:
1.Adopt degreasing and rust cleaning process before operate.
2.Shielding gas flow: 20-25L/min when welding
3.Extension: 15-25mm
4.The humidity of welding wire storage should be less than 60%
5.Storage period: Vacuum packaging less than 1 Year, other packaging less than half year.