ER308L 1.0/1.2/1.6/2.0/2.5/3.0 mm Stainless steel TIG Welding Wire
ER308/308L is used for welding types 304, 304L, 308, and 308L stainless steels. It is very similar to type 308, but has a carbon content held to a max of .03% to avoid carbide precipitation. This product can also be used for welding types 321 and 347 stainless steels. This wire is suitable for applications at cryogenic temperatures.
Introduction:
The main component of JQ.H00Cr21Ni10 is ultra-low carbon 18Cr-8Ni;
it is ultra-low C Stainless steel MIG welding wire. The
intergranular corrosion resistance of the weld metal is more
excellent. Welding smoothly, weld bead smoothly, excellent
corrosion-resistance, crack-resistance for acetic acid, sulfuric
acid, phosphoric acid and salt corrosion because it contains
Molybdenum.
Chemical Composition(%)
| Chemical Composition | C | Mn | Si | Cr | Ni | Mo | P | S | Cu |
| Guarantee Value | ≤0.030 | 1.00~2.50 | 0.30~0.65 | 19.50~22.00 | 9.00~11.00 | ≤0.75 | ≤0.030 | ≤0.030 | ≤0.75 |
| General Result | 0.024 | 1.72 | 0.48 | 19.76 | 9.83 | 0.006 | 0.018 | 0.010 | 0.06 |
Reference CURRENT (AC OR DC)
| Diameter (mm) | Φ1.6 | Φ2.0 | Φ2.5 | Φ3.2 |
| Welding Current (Amps) | 50~100 | 100~200 | 200~300 | 300~400 |
Notes:
1. Shielding gas: Adopt pure Argon gas. Recommendation flow rate:
9-14L/min (AMP 100-200A), 14-18L/min (AMP 200-300A).
2. Tungsten extension: 3-5mm, Arc length: 1-3mm.
3. Wind speed limited: ≤1.0m/s.
Argon gas shielding on back side of welding part will get better
welding result.
4. Mechanic property and metal anti-cracking ability of the welded
metal relative by energy pass value on the wire.
5. The welding should be operated in clean surface without rust,
moist, oil contamination and dust.
The above suggestions are for reference purpose. Evaluate and
determine the situation of the scene before starting the wielding
process.