We are professional 316L Modified(AISI 316LMOD,316L Mod,1.4435,724L,X2CrNiMo18-14-3) Forged Forging Check Control Globe Valve Body Bodies factory from china
The UREA 316L Modified grade has been specially developed for Urea
plant
applications. It is a 316L modified stainless steel with extra-low
silicon content and
substantial higher molybdenum contents.
The low carbon content, combined with a well balanced chemistry
(low silicon and
nickel content close to 14%) makes the alloy fully austenitic, free
of intermetallic
phase precipitations. The ferrite level is kept under 0.5% in the
solution annealing
and water quenched conditions.
The alloy is designed for improved corrosion resistance properties
in Urea-
carbonate environments.
EN 10088 / EN 10028................... X2 Cr Ni Mo 18-14-3 - 1.4435
AFNOR......................................... Z3 CND 18.14.03
DIN............................................... W.Nr 1.4435
ASTM. .......................................... 316L modified
The UREA 316L Modified grade is a fully austenitic stainless steel
which ferrite
content is guaranteed less than 0.5% after solution annealing heat
treatment
(1120°-1180°C (2048-2156°F) /water quenched). The carbon content is
kept low
while the steel making is optimised in order to improve the
cleanliness properties of
the steel.
The alloy is designed for urea applications (low carbon and silicon
contents).
Typical maximum corrosion results required following different
specifications after
Huey tests (ASTM A262 C - five periods of 48 h.) are : maximum
weight loss lower
than 3,3 µm/48 h (≈ 130 mg/dm² per 24 h.), with a maximum depth for
microcracks
of 200 µm in the long direction and 70 µm in the transverse
direction. The UREA
316L Modified grade behaves much better than those maximum values
as
indicated on the following graphs where 100 test results performed
between 1994
and 1996 are reported
Name & Description | Forging Handling Capacities | Quantity |
3150 Tons Free Forging Hydraulic Press | Max. Single Forging in 28 Tons | 1 |
5000mm Diameter Rolling Forging Machine | Max. Single Forging in 16 Tons | 1 |
8 Tons Free Forging Hummer | Max. Single Forging in 7.5 Tons | 1 |
6 Tons Free Forging Hummer | Max. Single Forging in 5.5 Tons | 1 |
5 Tons Free Forging Hummer | Max. Single Forging in 4.5 Tons | 1 |
60 Tons Forging Handling Operator | Max. Single Forging in 45 Tons | 1 |
10 Tons Forging Handling Operator | Max. Single Forging in 7.5 Tons | 1 |
80 Tons Crane | Max. Single Ingot in 80 Tons | 1 |
60/30 Tons Crane | Max. Single Ingot in 60 Tons | 1 |
30/10 Tons Crane | 30/10 Tons | 4 |
Trolley Heat Furnace | 5000*1500*1200 mm | 3 |
Trolley Heat Furnace | 8000*2000*1600 mm | 3 |
Trolley Heat Furnace | 6500*1500*1200 mm | 3 |
Vertical Heat Furnace | Ø2500*10000 mm | 2 |
Total Forging Equipment Quantity | 24 | |