China Steel continuous casting refractory manufacturer Slide Gate Plate for steel and iron plant ladle and tundish
Slide gate plate for Steel continuous casting is made of Tabular corundum, Resin, Zirconia, Carbon, Graphite, Bauxite as the main raw materials of shaped refractory products, the main component is Al2O3.
slide gate plate becomes more and more important in the process of modern steel smelting, becoming an indispensable part of smelting.It is in the process of continuous casting machine casting steel control device, can accurately adjust the water flow from the ladle in continuous casting tundish, the inflows and outflows of molten steel in balance, so that the continuous casting operation is easier to control.
Slide gate plates are made by Henan Hongtai after taking into account plant related conditions and specific operating conditions. The materials used for manufacturing slide gate plates are dependent upon grade of steel being produced, casting time, quantity of steel, and temperature of molten steel.
Our slide gate plate retain their shape and bore diameter is not affected by flow of molten steel. Slide gate plates made by Henan Hongtai posses many features that allow them to give high and consistent performance time after time.
Slide Gate Plates features are as follows.
Resistance to thermal shocks
Ability to resist corrosion caused by molten steel and slag
Resistance to abrasion
Low porosity and high bulk density
Great mechanical strength
Ability to withstand high temperatures
Ability to resist structural changes because of high operating
temperatures
Great resistance to oxidation
Smooth surface finish
China Steel continuous casting refractory manufacturer Slide Gate Plate for steel and iron plant ladle and tundish
Slide Gate Plate technical data:
| Index | Ladle Slide Gate Plate | |||
| Type | Al2O3-ZrO2-C | Al2O3-ZrO2-C | Al2O3-ZrO2-C | Al2O3-C |
| HBLTG-90 | HBLTG-80 | HBLTG-75 | HBLS-65 | |
| Raw material | Tabular corundum, Resin, Zirconia, Carbon, Graphite | Tabular corundum, Resin, Zirconia, Carbon, Graphite, Bauxite | Tabular corundum, Resin, Zirconia, Carbon, Graphite, Bauxite | Tabular corundum, Resin, Zirconia, Carbon, Graphite, Bauxite |
| Al2O3% Min | 90 | 80 | 75 | 65 |
| C% Max | 6.0 | 6.0 | 6.0 | 7.0 |
| ZrO2% Min | 4.0 | 4.0 | 4.0 | |
| A.P.% Max | 5 | 6 | 7 | 8 |
| BD% Min | 3.1 | 3.0 | 2.9 | 2.8 |
| C.C.S.MPA Min | 120 | 115 | 110 | 90 |
| HMOR Mpa (1400*30min) | 125 | 120 | 120 | |
| Service life(heats) | 4-8 (ironclad) | 2-4 | 2-3 | 1 |
| Service life depends on steel-making condition and differentconditions. | ||||
| The products can be customized as per your demands | ||||
China Steel continuous casting refractory manufacturer Slide Gate Plate for steel and iron plant ladle and tundish
Alumina-Carbon-Zircon Slide Gate Plate for Steel Ladles and tundish is a key component of a sliding nozzle, molten steel is direct control, determines a sliding nozzle member functions. The manufacturing process of the slide gate plate is different from the previous refractory materials.Flake Graphite Alumina-Carbon-Zircon Nozzle Slide Gate Plate for Steel Ladles has a molten steel injection function and a flow adjustment function.In addition to the processes of kneading, molding, firing, and inspection, there are also machining, installation and external processing of sliding surfaces. Overall adjustment process.
During use, due to long-term chemical corrosion and physical erosion of high temperature molten steel, severe and transient thermal shock and mechanical wear, the use conditions are extremely harsh; at the same time, in order to achieve free opening and closing of steel flow, the sliding surface is flat Strict requirements are required for the degree and plate size. Therefore, the slide gate plate must have the characteristics of high strength, wear resistance, slag resistance and good thermal shock stability.
China Steel continuous casting refractory manufacturer Slide Gate Plate for steel and iron plant ladle and tundish
Packaging of slide gate plate for steel ladle and tundish:
1.International standard seaworthy exportable packing.
2.Wooden pallet.
3.Wooden / bamboo case (box)..
4.Further packing information will be based on customer's
requirements.
Shipping details for slide gate plate for steel ladle and tundish:
1.The sample willl be send by International expresses
FEDEX/DHL/UPS/TNT.
2.The goods are transport by shipping.
Hot Sale Ladle Slide Gate Manufacturer with Competitive Price
Slide gate plate Payment Item :
1. Payment: T/T, Western Union,LC; Usually 30% deposits,70% balance
before delivery or negotiations to solve.
2. MOQ: Usually 1Tons
3. Quality Warranty: 1 years
Slide gate plate Delivery time :
1.Stocks:Within 5-7 days after receive the deposit.
2.Customization:Within 15-30 days after receive the deposite.
Jerry Li
Cell&WhatsApp: 0086-13373957739
Email: jerry(at)firebricks-supplies.com