Hot Blast Stove, Glass Furnace and Coke Oven Silica Brick, Quartz Fire Brick
Silica brick, quartz fire brick is made of silicon raw material with 93% silicon oxide. It has high refractoriness under load, good at acid slag erosion resistance.
Main characters of silica brick, quartz fire brick
(1)High refractoriness under load.
(2)High heat conductivity.
(3)Good thermal shock resistance.
(4)Solidity stable of capacity in high temperature.
Feature of silica brick, quartz fire brick
1.Strong acid slag resistance,
2.High refractoriness under load,
3.Volume shrinkage not change when reheated.
4.Used for glass furnace.
Hot Blast Stove, Glass Furnace and Coke Oven Silica Brick, Quartz Fire Brick
Technical date of silica brick, quartz fire brick
Please feel free to let us know your refractories needs, we will offer you the most suitable solution for you.
| Silica brick for glass furnace | |||||
| Item: | BG-96A | BG-96B | BG-95A | BG-95B | |
| SiO 2 | ≥96 | ≥96 | ≥95 | ≥95 | |
| Fe 2 O 3 | ≤0.8 | ≤1.0 | ≤1.2 | ≤1.2 | |
| Apparent porosity % | ≤22(24) | ||||
| Cold Crushing Strength MPa | Brick below20KG | ≥35(30) | |||
| Brick ≥20KG | ≥30(25) | ||||
| Refractoriness under load ºC | ≥1680 | ≥1670 | ≥1660 | ≥1650 | |
| True density g/cm ³ | ≤2.34 | ≤2.34 | ≤2.35 | ≤2.35 | |
| Silica brick for coke oven | ||
| Item: | CO-94A | CO-94B |
| SiO2: % | ≥94 | ≥94 |
| Al 2 O 3 : % | ≤ 1.5 | ≤ 1.5 |
| Fe2O3: % | ≤ 1.5 | ≤ 1.5 |
| Refractoriness under load 0.2Mpa | ≥ 1650ºC | ≥ 1650ºC |
| Apparent porosity: % | ≤ 22 | ≤ 24 |
| Bulk density: g/cm ³ | ≤ 2.34 | ≤ 2.35 |
| Cold crushing strength: MPa | ≥30 | ≥25 |
| Permanent linear change % (1450ºC ×2h) | 0~0.2 | 0~0.2 |
| Thermal expansion(1000ºC) | ≤1.28 | ≤1.30 |
| Silica brick for hot blast furnace | |
| Item | RG-95 |
| SiO2 | ≥ 95 |
| Al2O3 | ≤ 1.0 |
| Fe2O3 | ≤1.3 |
| Apparent porosity % | ≤22(24) |
| Cold crushing strength MPa | ≥45(35) |
| Remaining quarts % | ≤1.0 |
| Refractoriness under load ºC | ≥1650 |
| Creep(0.2Mpa ×1550ºC×50h) % | ≤0.8 |
| Thermal expansion coefficient (1000ºC) % | ≤1.25 |
| Apparent density g/cm ³ | ≤2.32 |
Hot Blast Stove, Glass Furnace and Coke Oven Silica Brick, Quartz Fire Brick
Application of silica brick, quartz fire brick
1.Glass melting furnace, ceramic frit kiln, sodium silicate furnace, soaking furnace, ceramic kiln, etc
2.Coke oven's coking chamber, combustion chamber walls, steel open-hearth's regenerator and sediment chamber, etc.
3.Load-bearing parts of high temperature hot blast stove and acid open-hearth furnace roof, etc.
Hot Blast Stove, Glass Furnace and Coke Oven Silica Brick, Quartz Fire Brick
Size of silica brick
Straight Type | Arch Type | Wedge Type |
L×W×H (mm) 230×114×65 230×114×75 230×114×32 220×110×60 220×110×50 220×110×40 220×110×30 | L×W×H/h (mm) 230×114×65/55 230×114×65/45 230×114×65/59 220×110×65/50 220×110×75/65 220×110×60/40 | L×W×H/h (mm) 230×114×65/55 230×114×65/45 220×110×75/65 220×110×60/40 |
Other Sizes Can Be Customized | ||
Hot Blast Stove, Glass Furnace and Coke Oven Silica Brick, Quartz Fire Brick
Hot Blast Stove, Glass Furnace and Coke Oven Silica Brick, Quartz Fire Brick
Production process of silica brick, quartz fire brick
1)Raw material to factory→checkout→burdening→stirring→mixing→taking
out the raw material,
2)Crushing→Mixing→Shaping→Drying→Firing→Inspection→Packaging and
Shipment.
2.Quality Assurance
1)Going out the furnace→checkout→packing→qualified product→putting
in storage→sale,
2)The process from raw to product are strictly tested by equipment.
1.Inspection and Control of incoming raw materials: according to
the chemical content,raw materials are classified into different
levels to ensure quality of brick first.
2.Inspection and control of the process: during the
production,every brick will be weighed twice strictly to reduce the
error of weight .
3.Quality audit by quality management: inspection of product
standardization of quality of each product by process control and
experimentation, taking corrective measures timely whenever
deviations are noted.
4.Before delivery, the inspectors will inspect the size,appearance,
physical and chemical properties of silica brick, quartz fire brick again in factory.