Products | Grade | SiO2 ≤% | CrO ≥ % | MgO ≥% | CaO ≤% | Bulk Density ≥ g/cm 3 | Apparent Porosity ≤ % | Cold crushing strength ≥ MPa | Refractoriness under load ≥(0.2Mpa) °C |
Direct-bonded magnesia-chrome brick | HT-12 | 1.5 | 12 | 65 | 2.98 | 18 | 40 | 1700 | |
HT-8A | 1.5 | 8 | 80 | 2.95 | 18 | 45 | 1700 | ||
HT-8B | 2.0 | 8 | 78 | 2.93 | 18 | 45 | 1650 | ||
HT-8C | 3.0 | 8 | 75 | 2.9 | 18 | 45 | 1600 | ||
Semi-bonded magnesia-chrome brick | HT | 3.5 | 6 | 72 | 2.95 | 18 | 40 | 1600 | |
Semi-bonded again magnesia-chrome brick | HT16 | 1.5 | 16 | 60 | 3.05 | 17 | 50 | 1700 | |
HT20 | 1.5 | 20 | 55 | 3.12 | 17 | 50 | 1700 | ||
Bonded again magnesia-chrome brick | HT16 | 1.4 | 16 | 60 | 3.05 | 16 | 50 | 1700 | |
HT20 | 1.5 | 20 | 55 | 3.12 | 16 | 50 | 1700 | ||
magnesia brick | HT-92 | 4.0 | 92 | 2.5 | 2.86 | 18 | 60 | 1570 | |
HT-95 | 2.0 | 94.5 | 2.0 | 2.92 | 18 | 50 | 1650 | ||
HT-97 | 1.2 | 96.5 | 1.5 | 2.98 | 17 | 50 | 1700 | ||
HT-98 | 0.6 | 97.5 | 1.2 | 3.02 | 17 | 50 | 1700 | ||
magnesia-alumina brick | HT-80A | 80 | 2.85 | 18 | 40 | 1600 | |||
HT-80B | 80 | 2.85 | 19 | 30 | 1580 | ||||
magnesia spinal brick | HT-80 | 1.0 | 80 | 2.95 | 18 | 45 | 1700 | ||
HT-75 | 3.0 | 75 | 2.85 | 19 | 40 | 1650 | |||
magnesia-zircon brick | HT-A | 77 | 3.05 | 17 | 60 | 1650 | |||
HT-B | 80 | 3.00 | 18 | 60 | 1630 |