Guangzhou Changfeng Steel Co., LTD |
|
D3 1.2080 SKD1 Cr12 Hot Rolled Alloy Die Steel Flat Bar
D3 Tool Steel is a high-carbon, high chromium, oilhardening tool
steel thatis characterized by a relatively high attainable hardness
and numerous, large, chromium-rich alloy carbides in the
microstructure. These carbides providegood resistance to wear from
sliding contact with other metals and abrasive materials.
AISI D3 alloy steel is heat treatable and will offer a hardness in
the range 58-64 HRC. After heat treatment D3 tool steel is hard,
durable and dense, and is immune from sinking in use. It offers a
measure of corrosion resistance when polished. In general, the
applications of AISI D3 tool steel resemble those of D2 tool steel
but it should be remembered that alloy tool steel D3 has better
wear resistance of the two steels and is preferred for such items
as shear blades. Owing to its higher wear resistance, AISI / ASTM
D3 cold work steel is slightly more difficult to grind than D2
steels.
1, Steel Grade:1.2080/ D3/ SKD1/Cr12 Cold Work Mould Steel
2, Specification
Chemical Compositons: | ||||||||
Grade | C | Si | Mn | P | S | Cr | W | V |
Cr12 | 2.00-2.30 | ≤0.40 | ≤0.40 | ≤0.030 | ≤0.035 | 11.50-13.0 | - | - |
D3 | 2.00-2.30 | 0.10-0.60 | 0.10-0.60 | ≤0.030 | ≤0.030 | 11.00-13.50 | ≤1.00 | ≤1.00 |
1.2080 | 1.90-2.20 | 0.10-0.60 | 0.20-0.60 | ≤0.030 | ≤0.030 | 11.00-13.50 | - | - |
SKD1 | 1.90-2.20 | 0.10-0.60 | 0.20-0.60 | ≤0.030 | ≤0.030 | 11.00-13.50 | - | - |
3,Size
Size of SKD1/1.2080 Cold Work Steel | |||
Round bar | Diameter(mm) | 12-300 | |
Plate | Thickness(mm) | Width (mm) | Length (mm) |
Max:800 | Max:1000 | Max:6000 |
4, Application
Used for making small impact,high quality wear cold-punching mould;
1)Used for high tolerance and long service life of all kinds of
cold stamping die and cold shear blade, thread rolling plate, etc.;
2)Tabletting punches and sleeves for corrosive;
3)Suitable for complex deformation of mould;
5, Features
1)High hardenability, high hardness, high wear resistance and good
toughness, quenching deformation, etc;
2)Good machinablity and inoxidizability;
3)Immune from sinking in use,high resistance to heavy pressure;
Forging of D3 Cold Work Tool Steel
Pre-heat at 900-950°C then raise temperature to 1050-1100°C. Soak
until uniformly heated. D3 tool steel is relatively hard at
elevated temperature. Therefore, initial hammer blows must be light
and the temperature must not be allowed to fall below 1020°C until
the metal begins to flow. Final forging should not be done below
900°C.
Heat Treatment of D3 Cold Work Steel
Heat Treatment
D3 tool steel requires hardening and tempering to achieve maximum
properties. For maximum accuracy, the parts of D3 tool steel should
be stress relieved after roughing operations. Stress should be
relieved at 648°C (1200°F) for one hour and cooled slowly.
Annealing
Heat D3 tool steels uniformly to 850-870°C, soak thoroughly, then
slow furnace cool at a rate of not more than 25°C per hour to
650°C. The parts may then be air cooled. This should result in a
maximum hardness of brinell 248.
Tempering
The D3 cold work steel should be cooled to room temperature and
should be tempered immediately. The parts should be placed in the
tempering furnace and increased slowly to the desired tempering
temperature. Tempering for 1 hour per inch of thickness is
required.
Hardening
D3 tool steel is extremely sensitive to overheating during
hardening - do not overheat.
Pre heat slowly to 800-850°C, the raise rapidly to 950-970°C and
soak until completely equalised. Quench in oil.
6, Delivery Days:
For abundant stock, 7-15 days.
For customized products, 15-30 days.
D3 1.2080 SKD1 Cr12 Hot Rolled Alloy Die Steel Flat Bar picture
show
7, Packing: Standard Export Packing or Customers' request
8, About Us
Guangzhou Changfeng Steel Co., Ltd. is a professional special steel company, which specializing in
this line in China since 2005. Our main products are Plastic Mould
Steel, Hot Work Mould Steel, Cold Work Mould Steel, Alloy
Structural Steel, Tool Steel, Stainless Steel, Carbon Steel and
Forged Block.
To ensure provide high quality products to customers, we have close
cooperation with many Chinese first class special steel
enterprises, including Baosteel Group, Dongbei Special Steel,
Changcheng Special Steel, Hongsheng Heavy Industry, Xingcheng
Special Steel and Daye Special Steel.