Hdpe double smooth geosynthetic membrane is consist by 97.5% high
density polyethylene material and about 2.5% carbon black and other
material.
Product Parameter
| Thickness | 0.25mm | 0.35mm | 0.5mm | 0.75mm | 1.0mm | 1.25mm | 1.5mm | 2.0mm |
| Density g/m2 | ≥0.94 | |||||||
| Tensile yield strength (N/mm) | 3.75 | 5 | 7.5 | 11 | 15 | 18 | 22 | 29 |
| Tensile breaking strength (N/mm) | 6.75 | 19 | 13.5 | 20 | 27 | 33 | 40 | 53 |
| Elongation at yield(%) | ≥12 | |||||||
| Elongation at break(%) | ≥700 | |||||||
| Puncture strength(N) | 80 | 150 | 160 | 240 | 320 | 400 | 480 | 640 |
| Angle tear load | 31.25 | 45 | 62.5 | 93 | 125 | 160 | 190 | 250 |
| Carbon black content(%) | 2.0-3.0 | |||||||
| 85℃ aging after 90 days high pressure | 55 | |||||||
| Material | high density polyethylene |
| Thickness | from 0.15mm to 3.0mm, or according customers' requirement |
| Color | green, black, white and transparent |
| Length | from 50m to 200m & customer ' s requirement |
| Width | from 1.0m to 8.0m, or according customers' requirement |
| Package | woven bag, or according customers' requirement |
| Surface | Smooth |
| Production Standard | ISO, GRI,ASTM,GB |
| Shipping Marks | support |
Properties | Test | Test Value | Testing | |||||||
| Method | Frequency | |||||||||
| 30 mils | 40 mils | 50 mils | 60 mils | 80 mils | 100 mils | 120 mils | (minimum) | |||
| Thickness mils (min. ave.) | D 5994 | nom. (-5%) | nom. (-5%) | nom. (-5%) | nom. (-5%) | nom. (-5%) | nom. (-5%) | nom. (-5%) | per roll | |
| · | lowest individual for 8 out of 10 values | -10% | -10% | -10% | -10% | -10% | -10% | -10% | ||
| · | lowest individual for any of the 10 values | -15% | -15% | -15% | -15% | -15% | -15% | -15% | ||
| Asperity Height mils (min. ave.) (1) | D 7466 | 10 mil | 10 mil | 10 mil | 10 mil | 10 mil | 10 mil | 10 mil | every 2nd roll (2) | |
| Density (min. ave.) | D 1505/D 792 | 0.940 g/cc | 0.940 g/cc | 0.940 g/cc | 0.940 g/cc | 0.940 g/cc | 0.940 g/cc | 0.940 g/cc | 200,000 lb | |
| Tensile Properties (min. ave.) (3) | D 6693 | 20,000 lb | ||||||||
| · | yield strength | Type IV | 63 lb/in. | 84 lb/in. | 105 lb/in. | 126 lb/in. | 168 lb/in. | 210 lb/in. | 252 lb/in. | |
| · | break strength | 45 lb/in. | 60 lb/in. | 75 lb/in. | 90 lb/in. | 120 lb/in. | 150 lb/in. | 180 lb/in. | ||
| · | yield elongation | 12% | 12% | 12% | 12% | 12% | 12% | 12% | ||
| · | break elongation | 100% | 100% | 100% | 100% | 100% | 100% | 100% | ||
| Tear Resistance (min. ave.) | D 1004 | 21 lb | 28 lb | 35 lb | 42 lb | 56 lb | 70 lb | 84 lb | 45,000 lb | |
| Puncture Resistance (min. ave.) | D 4833 | 45 lb | 60 lb | 75 lb | 90 lb | 120 lb | 150 lb | 180 lb | 45,000 lb | |
| Stress Crack Resistance (4) | D 5397 | 300 hr. | 300 hr. | 300 hr. | 300 hr. | 300 hr. | 300 hr. | 300 hr. | per GRI GM10 | |
| (App.) | ||||||||||
| Carbon Black Content (range) | D 4218 (5) | 2.0-3.0 % | 2.0-3.0 % | 2.0-3.0 % | 2.0-3.0 % | 2.0-3.0 % | 2.0-3.0 % | 2.0-3.0 % | 20,000 lb | |
| Carbon Black Dispersion | D 5596 | note (6) | note (6) | note (6) | note (6) | note (6) | note (6) | note (6) | 45,000 lb | |
| Oxidative Induction Time (OIT) (min. ave.) (7) | 200,000 lb | |||||||||
| (a) Standard OIT | D 3895 | 100 min. | 100 min. | 100 min. | 100 min. | 100 min. | 100 min. | 100 min. | ||
| — or — | ||||||||||
| (b) High Pressure OIT | D 5885 | 400 min. | 400 min. | 400 min. | 400 min. | 400 min. | 400 min. | 400 min. | ||
| Oven Aging at 85°C (7), (8) | D 5721 | |||||||||
| (a) Standard OIT (min. ave.) - % retained after 90 days | D 3895 | 55% | 55% | 55% | 55% | 55% | 55% | 55% | per each | |
| — or — | formulation | |||||||||
| (b) High Pressure OIT (min. ave.) - % retained after 90 days | D 5885 | 80% | 80% | 80% | 80% | 80% | 80% | 80% | ||
| UV Resistance (9) | D 7238 | |||||||||
| (a) Standard OIT (min. ave.) | D 3895 | N.R. (10) | N.R. (10) | N.R. (10) | N.R. (10) | N.R. (10) | N.R. (10) | N.R. (10) | per each | |
| — or — | formulation | |||||||||
| (b) High Pressure OIT (min. ave.) - % retained after 1600 hrs (11) | D 5885 | 50% | 50% | 50% | 50% | 50% | 50% | 50% | ||