Shenzhen Yurucheng Dental Materials Co., Ltd |
|
Open system Dental Zirconia HT High Strength Zirocnia Block for Coping
Dental Zirconia Disc
To achieve expected quality, the sintering curves must be followed.
Note: please employ high-temperature furnace specially designed for denture manufacturing. It is good for ceramics sintering to prolong heating up time and cooling time properly.
1. Sintering preparation: Make sure there is enough sintering space
to avoid deformation. After dyeing, the restoration must be dried.
Do not heat up too quickly for it might result in cracks. Make sure
the dust-proof cover is put on the crucible to keep impurity away
from restorations
2. After sintering: Following the instruction to lower temperature
and take out restorations. Do not reduce furnace temperature too
quickly to avoid cracks.
3.The highest temperature: the highest temperature will affect the translucency and dyeing results. Make sure the accurate temperature of every step. Sinter and preserve heat according to the instruction.
High Translucency Dental Zirconia Disc For Anterior Restorarion , Dental Zirconia Blank
YUCERA blanks are made from biocompatible zirconiumdioxyde. The
yttrium oxide stabilizing protects the material against cracks and
increases the tensile and compressive strength. The special grain
size allocation inside the material and the added aluminium oxide
also result in extra strength during milling and subsequently in
clinical use. The outstanding mechanical characteristics, excellent
chemical durability and the unbeaten biocompatibility combined with
the translucent color predestine XTCERA as the ideal material
provider for dental milling systems.
YUCERA HT translucency, apply to single crown, anterior teeth,
inlay/onlay and also veneers.
HT Dental Zirconia Disc
* High translucent
* Brilliant bending strength and economic block
* Suitable for coping and framework
Indications
Coping, Inlay, Onlay, Bridge, Crown
Physical Characteristics
Physical Characteristics |
Sintered density 6.07±0.01g/cm³ |
Bending Strength 1200 MPa |
Transmittance 41% |
Hardness 1200HV |
Sintering temperature 1480~1550℃/recommend 1530℃ |