Shanghai Siway Curtain Material Co., Ltd. |
|
|
SV-8800 Silicone Sealant for Insulating Glass with two component neutral-cure silicone sealant for insulating glass
High-quality silicone sealant tensile strength, tensile strength, anti-peel strength. Silicone sealant hardness and elasticity is moderate, too hard or too soft silicone sealant are not good silicone sealant
Two-component, neutral-cure, high modulus structural silicone
sealant
Excellent resistance to weathering
Excellent cohesiveness with most of construction material without
priming
Good compatibility with other neutral silicone sealant
The product A group is white,B group is black, A:B volume is
10:1,weight ratio is 14:1.the color is black after mixed.
Applicable to glass curtain wall structural glazing
Applicable to structural bonding glass curtain wall glass and metal
BASIC USES
SV8800 silicone sealant is designed for for insulating glass
TYPICAL PROPERTIES
These values are not intended for use in preparing specifications
Test item performance
index
Test
result
Individual
decision
droop
Vertical/mm ≦3 0
Level non- qualified
defrmation
nondefrmatio
n
Surface drying time ≦2h 40min qualified
Hardness/shore A 30~60 48 qualified
Elastic recovery/% ≧80 90 qualified
Tensile
adhesion
Tensile bond strength
/MPa
≧0.60 0.71
Ultimate tensile strength qualified
elongation/%
≧50 60
Bonding failure area ≦10 0
Adhesion at constant
extension
No
damage
No
damage
qualified
Water-
Tensile
adhesion after
uv treatment
Tensile bond strength
/MPa
≧0.45 0.68
Ultimate tensile strength qualified
elongation/%
≧40 99
Bonding failure area ≦30 0
Tensile
adhesion after
hot air aging
Tensile bond strength
/MPa
≧0.60 0.83
Ultimate tensile strength qualified
elongation/%
≧40 70
Bonding failure area ≦30 0
Thermal weight loss /
%
≦6.0 2.4 qualified
Remark
1,Adhesive backing;colorless and transparent and float glass
without
coating
2,No coating was found on the test specimens
3,Clear agent ;acetone
7 days after curing——25℃,50%R.H.
GB/T 531
Durometer Hardness Shore A 40
GB13477 The tensile modulus at 12.5%
elongation
Mpa 0.18
The ultimate tensile strength Mpa 0.92
GB13477 Elongation limit (fracture) % 150
CURE TIME
As exposed to air, SV8800 begins to cure inward from surface. Its
tack free
time is about 50 minutes; the full and optimal adhesion depends on
the
sealant depth.
Certification
GB-24266-2009;
Color
Component A(Base) – White, Component B(Catalyst)- Black
Package
1. Component A(Base): (190L), Component B(Catalyst) (18.5L)
2. Component A(Base):24.5kg (18L), Component B(Catalyst): 1.9kg (1.8L)
Shelf life
12 months
Note