Casting Cone Crushers Crusher Parts, Mantles For Cone Crushers Df018
Iron Casting Concaves & Mantles For Cone Crushers DF018 Crusher Wear Parts
Concaves & Mantles for Cone Crushers Feature:
1. Jaw plates for jaw crushers;
2. Hammers and impact plates for impact crushers;
3. Concaves and mantles for cone crushers.
Concaves & Mantles for Cone Crushers Description:
A. Jaw plates and cheek plates for jaw crushers;
B. Blow bars, hammers and impact plates for impact
crushers;
C. Concaves and mantles for cone crushers.
D. Depending on the specific working conditions, all wear
parts can be ordered as Manganese Steel, high Cr cast iron or Cr-Mo
Alloy Steel.
China crusher wear parts supplier provides crusher spare parts
services to worldwide crusher spares customer. Hope you find our
rock crusher parts process and impact crusher parts product
description helpful.
In the recent 10 years, our liners have been widely used in large,
medium and small ball mills in Chinese power generation, mining,
cement, Chemical engineering and metallurgical industries and super
fine pulverizing equipments. It is the only recommended liner
product in the latest standard of the electric-power industry in
China.
Technical Parameters
Taiyuan SIMIS Crusher Parts Branch Company
Chemical Composition & Mechanical Property of Wear-resistant
Castings
Item | Cr-Mo | Cr-Mo | Cr-Mo | High Cr white iron | High Cr Alloy Steel | High Manganese Steel | Ni-Hard cast iron |
C | 0.30~0.50 | 0.65~0.90 | 0.40~0.90 | 2.40~3.20 | 1.1~2.2 | 0.90~1.30 | 2.40~3.60 |
Si | 0.50~1.20 | ≤0.75 | 0.70~1.20 | 0.60~1.20 | 0.60~1.20 | ≤0.08 | ≤0.80 |
Mn | 0.40~1.20 | 0.50~1.20 | 0.60~1.00 | 0.50~1.00 | 0.50~1.00 | 11.00~18.00 | ≤2.0 |
Cr | 1.70~2.50 | 1.50~2.50 | 4.00~7.00 | 12.00~30.00 | 11.00~30.00 | 1.50~2.50 | 1.5~10 |
S | ≤0.04 | ≤0.06 | ≤0.04 | ≤0.04 | ≤0.04 | ≤0.04 | ≤0.15 |
P | ≤0.04 | ≤0.06 | ≤0.06 | ≤0.06 | ≤0.06 | ≤0.06 | ≤0.15 |
Mo | ≤0.5 | ≤0.5 | ≤0.5 | 0.10~3.0 | 0.10~3.0 | ≤1.0 | ≤0.10 |
Cu | 0.10~0.60 | ≤0.25 | 0.20~0.40 | 0.10~1.00 | 0.10~1.00 | - | - |
Ni | ≤0.50 | ≤0.30 | 0~0.30 | 0~0.30 | 0~0.30 | - | 3.3~10 |
Re | ≤0.02 | ≤0.02 | ≤0.02 | - | - | - | - |
Equivalent | DL/T 681-1999 | AS 2074 L2B Mod | DL/T 681-1999 | GB/T 8263-1999 | GB/T 5680-1998 | GB/T 8263-1999 | |
Material Type | Martensite Steel | Martensite or Pearlitic Cr Mo Steel | Martensite Steel | Martensite matrix | Austenitic Mn Steel | - | |
Hardness | HRc≥48 | HB470 & | HRc≥50 | HRc≥56 | HB≤300 | HRc≥56 | |
Impact Value | Ak≥40J | - | Ak≥10J | Ak≥4J | Ak≥80J | - | |
Our foundry has complete melting, heat treatment and test
equipments, such as mid-frequency induction electrical furnaces,
quenching and tempering furnaces, blast shot, spectrometer,
Rockwell and Brinell Hardness tester, impactor, UT tester and
metallographic microscope. We achieved the certificate of quality
management system ISO 9001:2008. We have been exporting castings to
overseas markets, such as Brazil, Australia and South Africa.