Metallized Electrical Ceramic Components Seal Rings Alumina Washers

Contact Us

[China]

Trade Verify

Address: Antaeus Industrial Park, Chuangye 1 Road, Loudi Economy and Technological Development Zone, Hunan, China

Contact name:Alice Deng

Loudi Antaeus Electronic Ceramic Co.,Ltd.

Verified Suppliers

Trust
Seal
Verified
Supplier
Credit
Check
Capability
Assessment

Metallized Electrical Ceramic Components Seal Rings Alumina Washers

Country/Region	china
City & Province	loudi hunan
Categories	Rare Earth & Products

Product Details

Alumina Seal Ceramic Rings / Industry Insulation Rings

1. Description:

Energy-saving advantages of alumina ceramics on heating components

High temperature co-fired alumina ceramic heating sheet, namely metal ceramics heater(hereinafter referred to as:MCH) uses high-temperature co-fired multilayer ceramic technology to print the heating resistor paste on the cast ceramic green body according to the design requirements of the heating circuit, and then multi-layers are combined and fired into a whole, so as to have corrosion resistance, high temperature resistance and longevity It has the advantages of long, high efficiency and energy saving, uniform temperature, good heat conduction, and fast thermal compensation. It does not contain harmful substances such as lead, mercury, and hexavalent chromium, and fully meets the EU environmental protection requirements.

2. Feature Advantages:

1) Refractory, High Temperature Resistance, Maximum Used Temperature: 1800 ºC (3272ºF)
2) Hardness Strength, Wear Resistance Up To Mohz 9.0 ; HRA 80-90
3) High Voltage, Good Insulation Performance ,Electrical Resistivity Up To 10∧14 Ohm.Cm
4) High Polished Surface Up To Rz0.8(Ra0.1)
5) Superior Mechanical Strength, MAX 10 MPa.m1/2 Fracture toughness
6) Pressure Resistance, Max 2300MPa compressive strength
7) Anti-High Corrosion Resistance, Such As Acid Alkali Resistance
8) Long Service Life
9) Other excellent property

3. Material Features / Properties:

Composite	(wt %)	99%	99.5%	99.8%
Color		White or Ivory	White or Ivory	White or Ivory
Density	g/cm 3	3.82	3.9	3.92
Hardness	HRA	83	85	85
Flexural Strength	Mpa (psi*10 3 )	375	386	381

4. Technical Parameters:

Technical Parameters of Ceramics
Items	Test Conditions	Unit or Symbol	99% AL2O3	95% AL2O3	90% AL2O3	Zirconia	Steatite	Silicon Carbide
Volume Density	--	g/cm3	≥3.70	≥3.62	≥3.40	≥5.90	≥2.60	≥3.08
Tightness	--	Pa·m³/s	≤1.0×10-11	≤1.0×10-11	≤1.0×10-11	-	-	-
Liquid Permeability	--	--	Pass	Pass	Pass		Pass	-
Flexural Strength	-	MPa	≥300	≥280	≥230	≥1100	≥120	≥400
Elastic Modulus	-	GPa	-	≥280	≥250	≥220	-	400
Poisson Ratio	-	-	-	0.20～0.25	0.20～0.25	-	-	-
Thermal Shock Resistance	800℃( Room Temperature) Cycle: 10 times		Pass	Pass	Pass	-	-	-
Coefficient of Linear Expansion	20℃～100℃	×10-6 K-1	-	-	-		≤8	-
	20℃～500℃	×10-6 K-1	6.5～7.5	6.5～7.5	6.5～7.5	6.5～11.2	-	-
	20℃～800℃	×10-6 K-1	6.5～8.0	6.5～8.0	6.3～7.3		-	4
	20℃～1200℃	×10-6 K-1	-	7.0～8.5	-	-	-	-
Coefficient of Thermal Conductivity	20℃	W/(m·k)	-	-	-	-	-	90～110
Coefficient of Thermal Conductivity	1000℃	W/(m·k)	-	-	-	-	-	90～110
Dielectric Constant	1MHz 20℃	-	9.0～10.5	9.0～10	9.0～10	-	≤7.5	-
	1MHz 50℃	-	-	9.0～10	-	-	-	-
	10GHz 20℃	-	9.0～10.5	9.0～10	9.0～10	-	-	-
Volume Resistivity	100℃	Ω·cm	≥1.0×1013	≥1.0×1013	≥1.0×1013	-	≥1.0×1012	-
	300℃		≥1.0×1013	≥1.0×1010	≥1.0×1013	-	-	-
	500℃		≥1.0×109	≥1.0×108	--	-	-	-
Disruptive Strength	D.C	kV/mm	≥17	≥15	≥15	-	≥20	-
Chemical Durability	1:9HCl	mg/c㎡	≤0.7	≤7.0	-	-	-	-
Chemical Durability	10%NaOH	mg/c㎡	≤0.1	≤0.2	-	--	-	-
Grain Size	-	μm	-	3~12	-	-	-	-

5. Process Flows:

Formulating --- Granulating --- Forming --- Sintering --- Grinding --- Printing --- Nickel Plating --- Assembing --- Brazing --- Inspecting --- Packing