The main process flow of cemented carbide round bar:
Milling → Recipe according to the application requirements → wet grinding → mixing → pulverization → drying → sieving → adding molding agent → drying again → sieving to make the mixture →
Granulation → pressing → forming → low pressure sintering → extrusion (blank) → cylindrical grinding (the blank does not have this process) → quality and size inspection → packaging
We provide high quality tungsten carbide rods with the following advantages:
1. 100% Virgin raw material
2. Advanced production equipment/test equipment (With HIP sintering).
3. With production experience over 10 years. We can make extruded tungsten carbide rod or die pressing tungsten carbide tube.
4. Standard length 100mm and 330mm, dia. from 0.5mm to 60mm, also can produce according to customers' request.
5. Competitive price and fast delivery
Application of Cemented Carbide Rods Blank
1. For making carbide mold punches
2. For making carbide core pins
3. For making carbide dental burrs
4. For making carbide PCB drills, drills, end mills & hole drilling tools, boring bar
5. For making carbide reamers.
The Features and the uses of cemented carbide
| Mark | ISO standard | Density g/cm³ | Hardness HRA | Bending strength ≥ MPa | Grain size | Features and notice | use |
| RX20 | K05 | 14.5 | 91.2 | 2100 | fine | Comprehensive properties, high hardness and high strength alloys widely used in woodworking field | Suitable for all types of wood processing, also for the processing of metal and non-metal materials |
| RX10T | K10 | 14.5 | 91.8 | 1800 | fine | The cutting edge is sharp and the wear resistance is very good. It is easy to crack at high temperatures. It is recommended to use high frequency induction welding or automatic welding machine. | It is suitable for the cutting of high-density boards, high-fiber boards and particleboards for woodworking tools. It is also suitable for finishing and semi-finishing of cast iron, non-ferrous metals and alloys. |
| RX10 | K10 | 14.75 | 90.5 | 2200 | medium | Good wear resistance and impact resistance, resistance welding can be used. | It is used for impact-resistant and nail-proof cutting of dry wood, cork, mixed wood and cement board, and is suitable for all types of forming knives in the furniture manufacturing industry. |
| YG6X | K10 | 14.9 | 90.8 | 1950 | fine | Good abrasion resistance | It is suitable for machining cold hard cast iron and heat resistant alloy, also suitable for finishing common cast iron. It is used to make casing cemented carbide tools and wear resistant parts. |
| YG6 | K20 | 14.95 | 90.5 | 2000 | medium | It has good wear resistance and impact toughness. Resistance welding can be used, but the welding temperature should not be too high. | It is suitable for the processing of ordinary cutting wood saws, cast iron aluminum profiles and copper rods. |
| YG8 | K20 | 14.80 | 89.5 | 2000 | medium | It has good wear resistance and impact toughness. Resistance welding can be used, but the welding temperature should not be too high. | It is suitable for the processing of non-ferrous metal profiles, dry wood, cork and hardware tools. Suitable for making ordinary sawtooth, it can also be used to make wear parts, general holes and metal processing. |
| YG8Ak | K20 | 14.75 | 90.0 | 2200 | medium | Wear resistance and hardness are good, resistance welding can be used, but welding temperature should not be too high. | Suitable for the processing of hardwood and ordinary wood |
| YG8C | K30 | 14.75 | 88.5 | 2300 | thick | Good impact toughness | Suitable for artificial marble, common wood with weeds, weeds and thickets. |