Carbide Band Saw Blade Forming Inserts Carbon Steel Saw Metal
Working Tools
Solid band saw forming inserts.
This carbide insert is used for sharp teething in saw blade machines. Materials are required to be highly wear-resistant and fracture-resistant.
Product verticality 0.01, size tolerance ISO 2768-f class
Recommended grades for metal working:
| Application Code | Chemical Composition | Physical Properties of powder | Physical and mechanical properties and mirco structure as stintered | Application recommended | ||||||||
| Co | Tic/ TacNbc | WC | Hall Flow | Apparent density | Density | Hardness | Transverse rupture strength | Coercivity | Magnetic saturation | Porosity | ||
| s/25cm3 | g/cm3 | g/cm3 | HV 30 | N/mm2 | KA/m | % | ||||||
| K05 | 6 | 0.3 | 93.7 | 35 | 3.45 | 14.94 | 1650-1750 | ≥1560 | 19.5-24.5 | 5.1-5.9 | A02 B02 | For machining super-hard grey cast steel, hardening steel, chilled iron, high silicon-aluminum alloy,high wear-resistant plastic, hard paper plate and ceramics. |
| 6 | 2 | 92 | 35 | 2.85 | 14.95 | 1350-1500 | ≥1600 | 21.5-26.5 | 4.9-5.9 | A02 B02 | ||
| K10-K15 | 6 | 0.4 | 93.6 | 35 | 3.45 | 14.91 | 1665-1835 | ≥123 | 19.5-24.5 | 5.2-6.2 | A02 B02 | For machining cast iron with hardness higher than 200HB, short-chip forgeable cast iron, silicon-aluminum alloy, copper alloy, plastic, glass, ceramics and stones. |
| K20 | 6 | 0.4 | 93.6 | 35 | 3.25 | 14.9 | 1600-1700 | ≥1670 | 16.3-19.2 | 5.2-6.0 | A02 B02 | For machining grey cast iron with hardness lower than 200HB, non-ferrous metal, copper, brass and aluminum |
| 7.8 | 1 | 91.2 | 35 | 3.35 | 14.61 | ≥1400 | ≥2000 | 15.0-18.0 | 6.6-7.8 | A02 B02 | ||
| K30 | 6 | 2 | 92 | 35 | 3.45 | 14.8 | 1450-1600 | ≥1320 | 13.5-15.1 | 5.3-6.0 | A02 B00 | For machining low-hardness grey cast iron, low-strength steel and compact wood. |