JIAXING VIIPLUS INTERNATIONAL TRADING CO.,LTD |
|
C93200(RG7)Bearing raw material supply,Tin bronze raw materials can be used in auto parts, bearings and other fields
Continuously cast OD up to 200 mm
CuSn7Zn4Pb7(GB/T 1176-1987)= G-CuSn 7 ZnPb(DIN)=C93200(SAE660 RG7)Chemical composition quality/% | |||||||||
Cu | Sn | Al | Fe | Mn | Ni | Pb | Si | P | Zn |
81.0-85.0 | 6.3-7.5 | 0.01 | 0.2 | - | 1 | 6.0-8.0 | 0.01 | 1.5 | 2.0-4.0 |
Note: The raw material contains lead, which has a high content and is likely to pollute the environment. Please use it according to the actual situation
Tensile Strength, | Yield Strength, at 0.5% Extension Under Load, | Elongation, in 2 in. or 50 mm min | Brinell Hardness (500 kg load) | Remarks | ||
---|---|---|---|---|---|---|
ksi | MPa | ksi | MPa | % | typical BHN | |
35 | 241 | 20 | 138 | 10 | 65 |
USA Customary | Metric | |
---|---|---|
material Melting Point - Liquidus | 1730 °F | 976 °C |
material Melting Point - Solidus | 1570 °F | 854 °C |
Density | 0.322 lb/in3 at 68 °F | 8.91 gm/cm3 at 20 °C |
Specific Gravity | 8.91 | 8.91 |
Electrical Conductivity | 12% IACS at 68 °F | 0.07 MegaSiemens/cm at 20 °C |
Thermal Conductivity | 33.6 Btu/sq ft/ft hr/°F at 68 °F | 58.2 W/m at 20 °C |
Coefficient of Thermal Expansion 68-212 | 10 · 10-6 per °F (68-212 °F) | 17.3 · 10-6 per °C (20-100 °C) |
Specific Heat Capacity | 0.09 Btu/lb/°F at 68 °F | 377.1 J/kg at 20 °C |
Modulus of Elasticity in Tension | 14500 ksi | 100000 MPa |
Product description: lead tin bronze
Pipe :25.4 to 406.4mm outside diameter
Rectangle: Maximum 508mm
Standard length :381mm
Shape/form: semi-finished product, coarse or nearly clean, anode, bar, billet/flower, square, hexagonal, plate, profile or
Structural type, flat/elongated