forged hastelloy c-4 rod

hastelloy c-4 c-22 c-276 c-2000 rod of low-carbon nickel-chromium- molybdenum alloys (UNS N10276, N06022, N06035, N06455, N06058, and N06059), low-carbon nickel-molybdenum- chromium-tantalum (UNS N06210), low-carbon nickel-chromium-molybdenum-copper alloy (UNS N06200), and low-carbon nickel-chromium-molybdenum-tungsten inconel 686 (UNS N06686), for use in general corrosive service

Rods 5/16to ¾ in. (7.94 to 19.05 mm), exclusive, in diameter, hot or cold finished, solution annealed and pickled, or mechanically descaled.

Rods ¾ to 3½ in. (19.05 to 88.9 mm), inclusive, in diameter, hot or cold finished, solution annealed, ground or turned.

Rods ¼ to 3 ½ in. (6.35 to 88.9 mm), inclusive, in diameter, solution annealed, cold finished, as cold finished, ground or turned (N06059 and N06686 only)

Chemical Requirements

Element

Composition Limits, %

Alloy N10276 Alloy N06022 Alloy N06455 Alloy N06059 Alloy N06058 Alloy N06200 Alloy N06210 Alloy N06686

Molybdenum 15.0–17.0 12.5–14.5 14.0–17.0 15.0–16.5 19.0 - 21.0 15.0–17.0 18.0–20.0 15.0-17.0

Chromium 14.5–16.5 20.0–22.5 14.0–18.0 22.0–24.0 20.0- 23.0 22.0–24.0 18.0–20.0 19.0-23.0

Iron 4.0–7.0 2.0–6.0 3.0 max 1.5, max 1.5, max 3.0 max 1.0 max 5.0 max

Tungsten 3.0–4.5 2.5–3.5 ... ... 0.3 max ... ... 3.0-4.4

Cobalt, max 2.5 2.5 2.0 0.3 0.3 max 2.0 max 1.0 ...

Carbon, max 0.010 0.015 0.015 0.010 0.010 0.010 0.015 0.010

Silicon, max 0.08 0.08 0.08 0.10 0.10 0.08 0.08 0.08

Manganese, max 1.0 0.50 1.0 0.5 0.5 0.5 0.5 0.75

Vanadium, max 0.35 0.35 ... ... ... ... 0.35 ...

Phosphorus, max 0.04 0.02 0.04 0.015 0.015 0.025 0.02 0.04

Sulfur, max 0.03 0.02 0.03 0.010 0.010 0.010 0.02 0.02

Titanium ... ... 0.7 max ... ... ... ... 0.02-0.25

Nickel remainderA remainderA remainderA Bal Bal remainderA remainderA remainderA

Aluminum ... ... ... 0.1–0.4 0.40 max 0.50 max ... ...

Copper ... ... ... 0.50 max 0.50 max 1.3–1.9 ... ...

Tantalum ... ... ... ... ... ... 1.5–2.2

Mechanical Property Requirements

Alloy Tensile Strength, min, psi (MPa)

Yield Strength (0.2 % Offset), min, psi

(MPa)

Elongation in 2 in.

(50.8 mm) or 4DA

min, %

N10276 100 000 (690) 41 000 (283) 40

N06022 100 000 (690) 45 000 (310) 45

N06455 100 000 (690) 40 000 (276) 40

N06058 110 000 (760) 52 000 (360) 40

N06059 100 000 (690) 45 000 (310) 45

N06200 100 000 (690) 41 000 (283) 45

N06686 100 000 (690) 45 000 (310) 45

N06210 100 000 (690) 45 000 (310) 45

Alloy Density

lb/in.3 g/cm3

N10276 0.321 8.87

N06022 0.314 8.69

N06455 0.312 8.64

N06058 0.318 8.80

N06059 0.311 8.60

N06200 0.307 8.50

N06686 0.315 8.73

N06210 0.316 8.76