forged hastelloy g-30 rod

Element

Composition Limits, %

Alloy N06007

Alloy N06975

Alloy N06985

Alloy N06030

Alloy N08031

Nickel

remainder

47.0–52.0

remainder

remainder

30.0-32.0

Chromium

21.0–23.5

23.0–26.0

21.0–23.5

28.0–31.5

26.0-28.0

Iron

18.0–21.0

remainder

18.0–21.0

13.0–17.0

remainder

Molybdenum

5.5–7.5

5.0–7.0

6.0–8.0

4.0–6.0

6.0-7.0†

Copper

1.5–2.5

0.70–1.20

1.5–2.5

1.0–2.4

1.0-1.4

Manganese

1.0–2.0

1.0 max

1.0 max

1.5 max

2.0 max

Cobalt, max

2.5

...

5.0 max

5.0 max

...

Carbon, max

0.05

0.03

0.015 max

0.03 max

0.015

Tungsten

1.0 max

...

1.5 max

1.5–4.0

...

Silicon, max

1.0

1.0

1.0 max

0.8 max

0.3

Phosphorus, max

0.04

0.03

0.04 max

0.04 max

0.020

Sulfur, max

0.03

0.03

0.03 max

0.02 max

0.010

Columbium + tantalum

1.75–2.50

...

0.50 max

0.30–1.50

...

Titanium

...

0.7–1.5

...

...

...

Nitrogen

0.15-0.25

...

...

...

...

Alloy

Specified Diameter, in. (mm)

Tensile Strength min, psi (MPa)

Yield Strength (0.2 % Offset), min, psi (MPa)

Elongation in 2 in. or 50.8 mm or 4D A min

N06007

5/16 to 3/4 (7.94 to 19.05), incl

90 000 (621)

35 000 (241)

35

Over 3/4 to 31/2 (19.05 to 88.9), incl

85 000 (586)

30 000 (207)

30

N06975

5/16 to 31/2 (7.94 to 88.9), incl

85 000 (586)

32 000 (221)

40

N06985

5/16 to 3/4 (7.9 to 19.05), incl

90 000 (621)

35 000 (241)

45

Over 3/4 to 31/2 (19.05 to 88.9), incl

85 000 (586)

30 000 (207)

35

N06030

...

85 000 (586)

35 000 (241)

30

N08031

All sizes

94 000 (648)

40 000 (276)

40