Aluminium Sheet 1mm Thick 5052 5754 5083
Product Description
The 5000 series of aluminium alloys represent 5052, 5005, 5083 and 5A05 series. The 5000 series aluminium bar belongs to the more commonly used alloy aluminium plate series, the main element is magnesium, the content of magnesium is between 3-5%. It can also be called Al-Mg alloy. Its main characteristics are low density, high tensile strength, high elongation and good fatigue strength, but it can not be strengthened by heat treatment. In the same area, the weight of Al-Mg alloy is lower than that of other series. It is also widely used in conventional industry. In our country, 5000 series aluminium sheet belongs to one of the more mature aluminium sheet series.
ALLOY | CHEMICAL COMPOSITION (%) | |||||||||||||
Si | Fe | Cu | Mn | Mg | Cr | Ni | Zn | Ti | Zr | Other | Al | |||
1035 | 0.35 | 0.6 | 0.1 | 0.05 | 0.05 | __ | __ | 0.1 | 0.03 | __ | 0.03 | __ | 99.35 | |
1100 | 0.95 | 0.05-0.2 | 0.05 | __ | __ | __ | 0.1 | __ | __ | 0.05 | 0.15 | 99 | ||
1050 | 0.25 | 0.4 | 0.05 | 0.05 | 0.05 | __ | __ | 0.05 | 0.03 | __ | 0.03 | __ | 99.5 | |
1060 | 0.25 | 0.35 | 0.05 | 0.03 | 0.05 | __ | __ | 0.05 | 0.03 | __ | 0.03 | __ | 99.6 | |
1070 | 0.2 | 0.25 | 0.04 | 0.03 | 0.03 | __ | __ | 0.04 | 0.03 | __ | 0.03 | __ | 99.7 | |
1080 | 0.15 | 0.15 | 0.03 | 0.02 | 0.02 | __ | __ | 0.03 | 0.03 | __ | 0.02 | __ | 99.8 | |
1045 | 0.3 | 0.45 | 0.1 | 0.05 | 0.05 | __ | __ | 0.05 | 0.03 | __ | 0.03 | __ | 99.45 | |
1145 | 0.15 | 0.3-0.5 | 0.02 | 0.05 | 0.05 | __ | __ | 0.1 | 0.03 | __ | 0.03 | __ | 99.35 | |
1200 | 1 | 0.05 | 0.05 | __ | __ | __ | 0.1 | 0.05 | __ | 0.05 | 0.15 | 99 | ||
1235 | 0.65 | 0.05 | 0.05 | 0.05 | __ | 0.1 | 0.06 | __ | 0.03 | __ | 99.35 | |||
2014 | 0.5-1.2 | 0.7 | 3.9-5.0 | 0.4-1.2 | 0.2-0.8 | 0.1 | 0.25 | 0.15 | 0.05 | 0.15 | rest | |||
2A12 | 0.5 | 0.5 | 3.8~4.9 | 0.3-0.9 | 1.2-1.8 | 0.1 | 0.3 | 0.15 | __ | 0.05 | 0.15 | rest | ||
2017 | 0.2-0.8 | 0.7 | 3.5-4.5 | 0.4-1.0 | 0.4-0.8 | 0.1 | 0.25 | 0.15 | 0.05 | 0.15 | rest | |||
2024 | 0.5 | 0.5 | 3.8-4.9 | 0.3-0.9 | 1.2-1.8 | 0.1 | 0.25 | 0.15 | 0.05 | 0.15 | rest | |||
3003 | 0.6 | 0.7 | 0.05-0.2 | 1.0-1.5 | 0.1 | 0.05 | 0.15 | rest | ||||||
3004 | 0.3 | 0.7 | 0.25 | 1.0-1.5 | 0.8-1.3 | __ | __ | 0.25 | __ | __ | 0.05 | 0.15 | rest | |
3104 | 0.6 | 0.8 | 0.05-0.25 | 0.8-1.4 | 0.8-1.3 | __ | __ | 0.25 | 0.1 | __ | 0.05 | 0.15 | rest | |
3105 | 0.6 | 0.7 | 0.3 | 0.3-0.8 | 0.2-0.8 | 0.2 | __ | 0.4 | 0.1 | __ | 0.05 | 0.15 | rest | |
5052 | 0.25 | 0.4 | 0.1 | 0.1 | 2.2-2.8 | 0.15-0.35 | __ | 0.1 | __ | __ | 0.05 | 0.15 | rest | |
5A06 | ≤0.40 | 0.000~0.400 | ≤0.10 | 0.50~0.8 | 5.8~6.8 | __ | 0.0001~0.005 | ≤0.20 | 0.02~0.10 | __ | 0.05 | 0.1 | rest | |
5005 | 0.3 | 0.7 | 0.2 | 0.2 | 0.5-1.1 | 0.1 | __ | 0.25 | __ | __ | 0.05 | 0.15 | rest | |
5050 | 0.4 | 0.7 | 0.2 | 0.1 | 1.1-1.8 | 0.1 | __ | 0.25 | __ | __ | 0.05 | 0.15 | rest | |
5154 | 0.25 | 0.4 | 0.1 | 0.1 | 3.1-3.9 | 0.15-0.35 | 0.25 | 0.2 | 0.05 | 0.15 | rest | |||
5754 | 0.4 | 0.4 | 0.1 | 0.5 | 2.6-3.6 | 0.3 | __ | 0.2 | 0.15 | __ | 0.05 | 0.15 | rest | |
5454 | 0.25 | 0.4 | 0.1 | 0.5-1.0 | 2.4-3.0 | 0.05-0.2 | 0.25 | 0.2 | 0.05 | 0.15 | rest | |||
5182 | 0.2 | 0.35 | 0.15 | 0.2-0.5 | 4.0-5.0 | 0.1 | 0.25 | 0.1 | 0.05 | 0.15 | rest | |||
5083 | 0.4 | 0.4 | 0.1 | 0.4-1.0 | 4.0-4.9 | 0.05-0.25 | _ | 0.25 | 0.15 | __ | 0.05 | 0.15 | rest | |
5086 | 0.4 | 0.5 | 0.1 | 0.2-0.7 | 3.5-4.5 | 0.05-0.25 | 0.25 | 0.15 | 0.05 | 0.15 | rest | |||
6060 | 0.3-0.6 | 0.1-0.3 | 0.1 | 0.1 | 0.35-0.6 | 0.05 | 0.15 | 0.1 | 0.05 | 0.15 | rest | |||
6061 | 0.4-0.8 | 0.7 | 0.15-0.4 | 0.15 | 0.8-1.2 | 0.04-0.35 | __ | 0.25 | 0.15 | __ | 0.05 | 0.15 | rest | |
6063 | 0.2-0.6 | 0.35 | 0.1 | 0.1 | 0.45-0.9 | 0.1 | __ | 0.1 | 0.1 | __ | 0.05 | 0.15 | rest | |
7075 | 0.4 | 0.5 | 1.2-2.0 | 0.3 | 2.1-2.9 | 0.18-0.28 | __ | 5.1-6.1 | 0.2 | __ | 0.05 | 0.15 | rest | |
8011 | 0.5-0.9 | 0.6-1.0 | 0.15-0.4 | 0.2 | 0.05 | 0.05 | __ | 0.01 | 0.08 | __ | 0.05 | 0.15 | rest | |
8079 | 0.05~0.3 | 0.7~1.3 | 0.05 | __ | __ | __ | __ | 0.1 | __ | 0.05 | 0.15 | rest |
Alloy | Temper | Thickness(mm) | Tensile strength(Mpa) | Yeild strength(Mpa) | Elongation(%) |
Min | |||||
5052 | H111 O | >0. 20 — 0. 50 | 170 — 215 | 65 | 12 |
>0. 50 — 1. 50 | 14 | ||||
>1.55 — 3.00 | 16 | ||||
>3. 00 — 6. 00 | 18 | ||||
>6.00 — 12. 50 | 165-215 | 19 | |||
>12. 50 — 50.00 | — | ||||
H12 | >0. 20 — 0. 50 | 210 — 260 | 160 | 4 | |
>0.5-1.5 | 5 | ||||
>1.50 —3.00 | 6 | ||||
>3, 00 — 6. 00 | 8 | ||||
H14 | >0. 20 — 0. 50 | 230-280 | 180 | 3 | |
>0.50-1.50 | 3 | ||||
>1. 50 -3. 00 | 4 | ||||
>3.00 — 6.00 | 4 | ||||