[China]
Trade Verify
Address: No. 1 South Jixiang Road, Guodian Town, Xinzheng, Zhengzhou, Henan, China 451100
Contact name:admin
Henan Jixiang Industrial Co., Ltd |
|
Verified Suppliers
|
|
|
Aluminum composite panel is made of aluminum alloy and plastic material to feature great hardness, light weight and smooth service, provided with wide range of sizes, shapes, colors, and styles to offer broader options for construction design, in a bid to better meet the requirements of contemporary construction on lightweight, elegant decoration and high hardness
Aluminum composite panel is widely used in all kinds of
architectural decorations for its excellent properties, such as
the, cladding, shops front, ceiling, counters, furniture, road
signs, billboards, kiosks, elevators, stores.
Product range:
| Surface Coating | Polyester Coating |
| Aluminum Alloy | AA1100, AA3003 |
| Aluminum Skin | 0.10mm,0.12mm,0.15mm,0.18mm,0.21mm,0.25mm,0.30mm |
| Panel Thickness | 2mm,3mm,4mm,5mm |
| Core Material | Non-toxic low density polyethylene |
| Panel Width | 1000mm,1220mm,1250mm,1500, |
| Panel Length | 2440mm,3050mm,4000mm,5000mm |
| Back Coat | PE coating, Primer Coating ,Mill finish |
Products tolerance:
| Panel Width | ±2mm |
| Panel Length | ±3mm |
| Panel Thickness | ±0.2mm |
| Panel Diagonal | ≤ 5mm |
| Aluminum layer thickness | ±0.02mm |
Technical data:
| Description | Test standard | Polyester |
| Coating Thickness (μm) | Polyester paint >=16μm | 16μm to 18μm |
| Coating flexibility (T-bend) | Polyester paint ≤ 3T | ≤ 3T |
| Color different | ΔE<=2.0 (follow color sample) | ΔE<=2.0 |
| Pencil hardness | >=HB | >=2H |
| Chemical resistance | 2%HCI or 2%NaOH test in 24 hours -No change | No change |
| Coating adhesion | >=1grade for 10810mm2 gradding test | 1grade |
| Resist solvent | 100 times without change | No change |
| Boiling water resistance | 2 hours without change | No change |
| Peeling strength/stripping strength | Average >=5N/mm of 180oc peel off for panel with 0.21mm alu.skin | 5N/mm |
| Impact test for paint | 20KG.cm impact-paint no split for panel | No split |
| Abrasion resistance (L/Mil) | NIL | NIL |
| Temperature resistance | -40ºC to +80ºC temperature without change of color difference and paint peel off, peeling strength average dropprate<=10% | Change of glossy only, no paint |
| Peel off | ||
| Coefficient of linear Thermal Expansion | 100ºC temperature difference | 2.4mm/n |
| Detergent resistance (3%) | ASTM D2248 | No change |
| Humidity Resistance (3000hrs,100%RH,100°F) | ASTM D2247 | No change |
| Salt spray resistance (3000hrs,5% salt) | ASTM B117 | No change |
| Resistance to Staining | 600h radiate in 800W/M2 in humidity condition ,glossiness deviation less grade 2,color difference <=4.0 | No change |