20MnV6 Hollow Bar
What's the 20MnV6 Hollow Bar specification, 20MnV6 Hollow Bar chemistry, 20MnV6 Hollow Bar equivalent, 20MnV6 Hollow Bar Mechanical Properties? 20MnV6 Hollow Bar manufacturer in China.
What is 20MnV6
20MnV6 is a carbon-manganese steel micro alloyed with vanadium, generally
supplied in the black hot rolled condition with
a typical tensile strength range of 600 - 790 Mpa and a high
typical yield strength range of 440 - 570 Mpa.Characterized by
excellent machinability due to silicon - calcium treatment and
precise control of the sulphur content, excellent weldability
with high yield and tensile strengths due to the micro - alloying
effect of the vanadium.The low carbon content and the
vanadium addition allows surface hardening by carburising,
carbonitriding or nitriding. It will also respond to high or
medium frequency induction hardening and can be through hardened
and tempered producing a moderate improvement in
tensile and yield strength, this varying depending upon wall
thickness.20MnV6 hollow bar is used extensively by all
industry sectors for a wide range of applications utilizing it's
considerable saving on machining time and weight over solid
bar.
20MnV6 Typical applications are: Bushes, Cylinders Various, Conveyor Rolls, Hollow Shafts, Hollow
Parts and components, Nuts,
Rings, etc.
20MnV6 Related Specifications
Europe EN 10294-1
France NF A49312 20MV6
Germany W.Nr 1.5217 20MV6
W.Nr 1.8905 StE 460
Great Britain BS4360 GR 55
USA UNS K01907 and K12202
20MnV6 Chemical Composition (Base Material)
| Min % | Max % |
Carbon | 0.16 | 0.22 |
Silicon | 0.10 | 0.35 |
Manganese | 1.130 | 1.60 |
Vanadium | 0.08 | 0.15 |
Phosphorous | 0 | 0.03 |
Sulphur | 0.02 | 0.04 |
20MnV6 Mechanical Property Requirements - As Supplied in the Black Hot Rolled Condition |
Tensile Strength Mpa Min. Wall Thickness (mm) | <16 | 620 |
<25 | 310 |
>25 | 550 |
0.2% Yield Strength Mpa Min. Wall Thickness (mm) | <16 | 470 |
<25 | 460 |
<30 | 430 |
<40 | 420 |
<50 | 410 |
<70 | 400 |
Elongation on 5.65√S0 % Min | 18 |
Hardness Brinell Min | 180 |
Typical Mechanical Properties - As Supplied in the Black Hot Rolled
Condition |
Tensile Strength Mpa | 690 | |
Yield Strength Mpa | 500 | |
Elongation % | 21 | |
Hardness HB | 210 | |
Typical (Minimum) Mechanical Properties - Water Quenched at 925 oC and Tempered at 580 oC. |
Tensile Strength Mpa Wall Thickness (mm) | <20 | 750 |
<25 | 700 |
<30 | 650 |
0.2% Yield Strength Mpa Min. Wall Thickness (mm) | <20 | 650 |
<25 | 620 |
<30 | 570 |
Elongation % Wall Thickness | <20 | 16 |
>20 | 17 |
Impact +20oC 0oC -20oC J | | 40 |
| 32 |
| 28 |
20MnV6 Carbonitriding
Heat to 870 oC - 880 oC in a gaseous media consisting of carbon
monoxide/hydrocarbon plus ammonia, hold for sufficient
time to develop the required case depth, carbon and nitrogen
content, followed by quenching in oil or water as required.
Typical case hardness achieved up to Rc 60.Tempering immediately
while still hand warm at 150 oC - 200 oC will reduce
stresses and improve the toughness of the case.
20MnV6 Carburizing
Pack, salt or gas carburise at 880 oC - 920 oC, holding for
sufficient time to develop the required case depth and carbon
content, followed by a suitable heat treatment cycle to optimise
case and/or core properties.Typical case hardness
achieved up to Rc 63.
20MnV6 Case Hardening
Water quench from 760 oC - 780 oC.
20MnV6 or Core Refining
Oil quench from 870 oC - 880 oC prior to water quench as
above.Tempering immediately following water quench at 150 oC -
200 oC will reduce stresses and improve toughness of case.