Product Name :
Carbon AISI/SAE 1040-1045 (UNS G10400-G10450)
- a Special Bar Quality Medium-Carbon Machinery Steel
Characteristics
− General purpose, fine grain, machinery steel suitable for a wide
range of applications in the condition as supplied - approximately
90,000 psi (620 N/mm2) depending on the size of section. This steel
is primarily water- hardening, but may also be quenched in oil.
Excellent wear resistance can be obtained by flame or induction
hardening. Care required if welding, due to higher carbon content.
Good machinability
Typical Applications
− Shafts, axles, spindles, bolts, lightly stressed gears, machined
parts of all types.
Typical Heat Treatment
− Forging – Commence 1150˚C Max finish 925⁰C.
− Annealing – 800˚ to 830˚C Surface cool
− 870/ 915˚C air Cool
− Normaling – 830˚C to 850˚C water quench
− Hardening – 850˚C to 870˚C oil quench.
− Tempering – 425˚C to 870˚C according to properties
Mechanical Properties
− Typical – as supplied
− Tensile Strength – 90,000 psi (620 N/mm2)
− Yield Strength – 23,000 psi (410 N/mm2)
− Elongation – 25%
− Reduction of Area – 50%
− Hardness – HB 201
− Machinability – 65
Carbon AISI/SAE 1018 COLD FINISHED (UNS G10180)
- Cold Drawn '20' Carbon Steel, available in all bar sections
Characteristics
− Most cold finished bars are produced by cold drawing oversize hot
rolled bars through a die. The cold reduction of the bar results in
significantly improved mechanical properties, with a smooth surface
finish to close tolerances. The cold working of the bar likewise
improves machinability, usually rated at 76. Larger bars are often
produced by turning and polishing only. In this case, the
properties of the steel are not improved and remain the same as the
original hot rolled, special quality bar. The product is easy to
weld and readily responds to carburizing. Cold finished product is
manufactured in conformance to ASTM A108
Typical Applications
− All forms of shafting and machinery parts. When carburized
-gears, pinions, king pins
Carbon AISI/SAE 1018 COLD FINISHED
(UNS G10180)
Size Tolerances –Rounds Tolerances
- all tolerances are MINUS
11/2" dia. (38.1 mm) and under
Minus 0.002” (.050 mm)
Over 1 1/2" dia. to 2 1/2" dia (63.5 mm)
Minus 0.003” (.075 mm)
Over 2 1/2" dia. to 4" dia (101.6 mm)
Minus 0.004” (.100 mm)
Over 4" dia. to 6" dia (152.4" mm)
Minus 0.005” (.125 mm)
Over 6" dia. to 8" dia (203.2 mm)
Minus 0.006” (.150 mm)
Carbon 1018
Characteristics
− Produced to the requirements of ASTM A576 , this special bar
quality, low-carbon machinery steels, is extremely versatile. It
machines well and is easily weldable. The steel grade can be
carburized
Typical Applications
− Bearing in mind the tensile strength of approximately 60,000 psi
(414 N/mm2), the steel is suitable for a wide variety of general
engineering parts, shafts, studs, bolts, tie-rods etc
Mechanical Properties
− Typical as supplied
− Tensile Strength – 58,000 psi
− 2Tensile Strength – 400 N/mm2
− Yield Strength – 32,000 psi
− 2Yield Strength – 220 N/mm2
− Elongation – 25%
− Reduction of Area – 50%
− Hardness – HB 116
Comment
− This product may also conform to the requirements of ASTMA36
complete with the mechanical property requirements detailed below
− Tensile Strength – 58,000 – 80,000 psi
− Yield Strength – 36,000 psi minimum, 250 Mpa minimum
− Elongation minimum – 20%
Aluminum Extrusions
Aluminum Squares and Rounds Only 6061
Bronze Aluminum Bronze Alloy 954
Characteristics
− Produced conforming to ASTM B505, Alloy 954 Aluminum Bronze is
produced oversized to finish, machine to the nominal size ordered.
− Density: 0.340 lb/in3 at 68ºF; 9.41 g/cm3 at 20ºC
Mechanical Properties
− Yield – 35,000 psi
− Tensile Strength – 85,000 psi
− Elongation – 18%
− Hardness – 140-170 HBN
Bronze SAE660 Bearing
Characteristics
− Produced conforming to ASTM B505, SAE660 Bearing Bronze
(Bars and Tubes). Produced oversized. to finish, machine to the
nominal size ordered.
− Density: 0.322 lb/in3 at 68ºF; 8.91 g/cm3 at 20ºC
Typical Applications
− Industrial Machinery & Equipment Market: In-plant Equipment,
Industrial Valves & Fittings, Turbines, Off-highway Vehicles
− Products: Bushings, Plumbing Valves, Air Brakes, Brass Anodes for
Plating, Brass Plating of Steel Belts in Tires, Wear Plates in
Cranes, Hydraulic Seals, Gears, Bearings, Valve Stems, Turbine
seals, Flanges
− Transportation Equipment Market: Automotive Non-electrical,
Railroad, Marine, Aircraft
− Products: Motors, General Hardware, Carburetor Assemblies,
Fittings
− Military Market: All Specified Military Applications
− Water Handling Equipment: Alloys used in Marine service and
products such as seawater piping, pumps, valves, etc
− Special Market (Fastest Growing Market) Products: Food Processing
Equipment, Hydraulic Seals, Plumbing Valves, Wear Plates and Guides
Mechanical Properties
− Yield – 18,000 psi
− Tensile Strength – 35,000 psi
− Elongation – 20%
− Hardness – 60-70 HBN
Characteristics
− This is the least expensive and most versatile of the
heat-treatable aluminum alloys and offers a good range of
properties. It is generally selected where welding or brazing is
required and for its high corrosion resistance
Typical Applications
− General engineering and structural components. Trucks and
trailers. Boats.
− Furniture. Pipe fittings. Miscellaneous parts requiring good
corrosion resistance.
Mechanical Properties
− Minimum Properties:
− UTS Yield – 38 ksi, 35 ksi
− Elongation in 2” – 8%-10%
− Typical Properties:
− UTS Yield – 45 ksi, 41 ksi
− Elongation in 2” – 12%-17%
− Shear Strength – 30 ksi
OCTG (OLAJ ÉS GÁZIPARI, PETROKÉMIAI CSÖVEK), ÉGHETŐ ANYAGOK
VEZETÉSÉRE
ALKALMAS CSÖVEK
OCTG azaz az un. éghető anyagok vezetésére alkalmas csöveket
elsősorban olaj és gázipar számára forgalmazzuk,
csővezeték építéshez, szerelési és karbantartási munkákhoz hossz
hegesztett és spirál hegesztett kivitelben. Ezen termékeket
kombinálni tudjuk csőszigeteléssel is.
Méretválaszték: Ø 21,3-3500 mm
Szabványok: EN 10208-1, EN 10208-2
Minőségek: L245MB/NB, L290MB/NB, L360 MB/NB, L290 NB/MB, L415
NB/MB, L210GA, L235GA, L245GA, L290GA,
L360GA
Hosszak: 4-13 (20) m
OCTG (OIL, GAS, PETROCHEMICAL TUBES), TUBES SUITABLE FOR CONDUCTING
COMBUSTIBLE MATERIALS
We deal with our OCTG tubes (so called tubes suitable for
conducting flammable materials) mainly for the petrochemical
oil and gas industry for big and smaller line pipe, maintenance
project sin spirally welded and longitudinally welded typs.
Thes eproducts can be cominated with isolation and coatings.
Size assortment: Ø 21,3-3500 mm
Standards: EN 10208-1, EN 10208-2
Qualities: L245MB/NB, L290MB/NB, L360 MB/NB, L290 NB/MB, L415
NB/MB, L210GA, L235GA, L245GA, L290GA, L360GA
Lenghts: 4-13 (20) m
API 5CT J55 oil casing seamless pipe Steel Grades: K55, J55, L80-1
,N80,C90,C95, P110, T95
Standard: API 5CT, API 5D
Steel Grades: K55, J55, L80-1 ,N80,C90,C95, P110, T95
Size: 2 3/8"-4 1/2"*0.167"-0630"
Casing Pipe
Tubing steel pipe
Oil Casing Pipe/Steel Pipe
Including ordinary casing, Anti-collapse casing, Anti-corrosion
casing, Hi-strength casing
Serves as walls of a well;
Standard: API 5CT
Steel Grades: k55, J55, L80,N80,C90,C95, P110 T95,
M65,E75,X95,G105,S135
1) Tubing
OD: 2 3/8" -----4 1/2"
WT: 0.167" -----0.630"
Note: P : Plain end, N: Non upset, U: External upset, T&C:
Threaded and coupled.
2) Casing
OD: 2 3/8“ ----20"
WT: 0.205" --- 0.5"
Note: P: Plain end, S: Short round thread, L: Long round thread
Length
R1 R2 R3
Tubing 6.10 -7.32 m 8.53-9.75m 11.58-12.80m
Casing 4.88 - 7.62m 6.72 -10.36m 10.36 - 14.63m
3) Drill Pipe
OD: 2 3/8" - 5 1/2"
WT: 0.280" - 0.449"
Note: EU: External upset , IEU: Internal & External upset
Thread of tool joint are right-hand or left hand
Welded Casing and Tubing
Produced at Camrose, Calgary, Red Deer, and Regina.
Grades
- API 5CT H40, J55, L80, N80 and P110; and proprietary E80.
Diameters
- 2 3/8 - 16 in (60.3 - 406.4 mm)
Wall Thickness
- 0.190 - 0.545 in (4.8 - 13.8 mm)
Lengths
Seamless Casing
FEATURING New Proprietary Seamless Casing Products!
Produced at Pueblo.
Grades
- API 5CT N80, L80, P110 and proprietary CF95.
- Proprietary ENA 80-SS
- Proprietary ENA Q125-HCl
Diameters
- 7 - 9 5/8 in (177.8 - 244.5 mm)
Wall Thickness
- 0.317 - 0.595 in (8.5 - 15.1 mm)
API Oil pipe, Casing pipe
| Type | Label 1 (in) | Outside diameter (mm) | Wall thickness (mm) | Grade | Type of thread | Length |
| Casing | 4-1/2 | 114.30 | 5.21-8.56 | H40-P110 | STC LC BC | 4.88-13.5m |
| 5 | 127.00 | 5.59-12.70 | H40-P110 |
| 5-1/2 | 139.70 | 6.20-22.22 | H40-P110 |
| 6-5/8 | 168.28 | 7.32-12.06 | H40-P110 |
| 7 | 177.80 | 5.87-22.22 | H40-P110 |
| Oil pipe | 2-3/8 | 60.32 | 4.24-8.53 | H40-P110 | NU EU | 6.1-12.8m |
| 2-7/8 | 73.02 | 5.51-11.18 | H40-P110 |
| 3-1/2 | 88.90 | 5.49-13.46 | H40-P110 |
| 4 | 101.60 | 5.74-15.49 | H40-P110 |
| 4-1/2 | 114.30 | 6.88-16.00 | H40-P110 |
| Grade | Yield Strength(Mpa) | Tensile Strength(Mpa) | Hardness |
| J55 | 379-522 | >517 | |
| K55 | 379-552 | >655 | |
| N80 | 552-758 | >689 | |
| L80-1 | 552-655 | >689 | 23-241 |
| C90 | 621-724 | >689 | 25.4-255 |
| C95 | 655-758 | >724 | |
| T95 | 655-758 | >724 | 25.4-255 |
| P110 | 758-965 | >862 | |
API 5CT J55 oil casing seamless pipe Pictures