The PIPE Multi-ply Textile Conveyor Belt is made from the finest quality textile and rubber materials, which provides excellent resistance to abrasion. This makes it ideal for handling abrasive materials such as gravel, sand, and minerals without causing any damage to the belt. The abrasion resistance of this belt ensures a longer lifespan, reducing the need for frequent replacements and saving costs in the long run.
Characteristics
1.Enclosed conveying of materials, protecting both the materials and the environment.
2.Steep angled conveying, the conveying angle can reach 30° usually.
3.Conveying line can be arranged according to the curve of space.
Technical details
1. Fabric core material: Usually polyester, nylon and other
high-strength fiber materials.
2. Conveyor belt thickness: designed according to different
application requirements and load capacity.
3. Covering material: such as rubber, PVC, etc., to provide
wear-resistant and anti-slip performance.
Standard Specifications
Strength(KN/m) | No. Of Piles | Carcass Type | Belt Width | Pipe diameters (mm) |
300 | 2-4 | NN/EP |
500-2400mm | 100 150 200 250 300 350 400 450 500 550 600 |
400 | 2-4 | NN/EP | ||
500 | 2-5 | NN/EP | ||
630 | 3-6 | NN/EP | ||
800 | 3-6 | NN/EP | ||
1000 | 3-6 | NN/EP | ||
1250 | 3-6 | NN/EP | ||
1400 | 3-6 | NN/EP | ||
1600 | 4-6 | NN/EP | ||
2000 | 4-6 | NN/EP |
Note: It can be customized according to customers’ requirements.
Covers grades
In accordance with HG/T 4224-2011 standard
Grade | Tensile strength min. (ISO37) Mpa | Elongation at break (ISO37) % | Abrasion max. (ISO4649) mm³ | Change of tensile strength and elongation at break after hot air aging % |
H | 25 | 450 | 120 | -25 ~ +25 |
D | 18 | 400 | 90 | -25 ~ +25 |
L | 20 | 400 | 150 | -25 ~ +25 |
1.Ozone resistant test condition: (50±5)pphm, 40±2℃, elongation: (20±2)%, time 96hours. 2.Hot air aging test condition:70℃×168h |
The values will help to determine the appropriate cover compound for the application or for the materials carries. Reliable assessment of the behavior of the covers in service for wear and cut resistance cannot be determined from tensile strength, and abrasion values alone.