Poly(vinyl acetate) adhesive Glue WPPD3 Wood Working PVA Glue For Wood Working Flooring Adhesive Wood Glue white glue
| WPPD3 Series | |
| Commodity: | WPPD3 Wood Working PVA Glue For Wood Working Flooring Adhesive Wood Glue white glue |
| Other Names:: | Water Based Polymer-isocyanate Adhesives For Joining Wood |
| Type:: | Liquid Glue |
| Classification:: | Volatile Solvent Adhesives |
| Usage:: | Construction, Fiber & Garment, Footwear , Packing, |
| Main Raw Material:: | POLYURETHANE |
| Application:: | PVAC Glue For Wood Assembly |
| Shelf Life:: | 9 Months In Original Closed Container |
| Feature:: | Good Water Resistance And Excellent Curing Spped |
| Packing:: | 20 Kgs Per Barrel,30 Kgs/barrel, 10 Kgs/barrel |
| The Amount Of Cloth Glue:: | 150-200 G/m2 |
| Pressurizing Pressure:: | 7.0-10.0 Kg/cm² For Low-density Materials, 9.0-12.0 Kg/cm² For Medium-density Materials, 12.0-17.0 Kg/cm² For High-density Materials |
| Pressurization Time:: | The Ambient Temperature Is Above 25℃, And The Moisture Content Of The Material Is 8-12% |
water based polymer-isocyanate adhesives for joining wood
Product introduction:
One-component puzzle glue is polyvinyl acetate adhesive, referred
to as PVAc adhesive, and its English name is Poly(vinyl acetate)
adhesive or modified latex. The main component is polyvinyl
acetate, which is polymerized from vinyl acetate monomer.
Macromolecular substances.
Application range:
Suitable for window frame components, solid wood panels, floors,
2-layer composite floors (glued floors), etc.
Jigsaw glue-single-component jigsaw glue model parameter list:
| Product name | PH | Solid content/% | Viscosity/25℃ | colour | Characteristics and applicability |
| PG95 | 3±1 | 50±2 | 17000±2000 | Brown | D3 waterproof grade modified PVAC latex, fast curing speed, good permeability and tensile strength, suitable for assembly of various process structures, and can also be used for applications such as D3 waterproofing requirements. |
| PG80 | 3±1 | 54±2 | 18000±3000 | White | D3 waterproof grade modified PVAC latex, fast curing speed, good permeability and tensile strength, suitable for assembly of various process structures, and can also be used for applications such as D3 waterproofing requirements. |
| PG52 | 3±1 | 52±2 | 15000±2000 | light yellow | D3 waterproof grade modified PVAC latex has fast curing speed, good filling property, good solvent resistance and moisture resistance. It is suitable for assembly of various process structures and can also be used for applications such as D3 waterproofing requirements. |
| PG30L | 3±1 | 48±2 | 4000±1000 | White | D3 waterproof grade modified PVAC latex, fast curing speed, good permeability and tensile strength, suitable for assembly of various process structures, and can also be used for applications such as D3 waterproofing requirements. |
Features
1. Easy to operate: Water-based environmentally friendly products
that meet the global formaldehyde content limit requirements.
2. Ten-ring certification, European standard, Japanese JAS standard
environmental protection product, high shear strength, fast curing
speed, can meet the strength application of indoor wood product
manufacturing process.
Application notes
1. The moisture content of wood is 8-12%, and the high moisture
content needs to double the pressing time. Too high wood moisture
content will cause cracks due to shrinkage during the drying
process.
2. In order to obtain a significant effect, the surface of the wood
must be planed. In order to obtain better gluing strength, gluing
should be implemented within 24 hours after wood planing. For wood
with oily or resin content, gluing should be implemented within 4
hours after wood planing.
3. After pressing, check whether the glue is evenly squeezed out of
the glue line to determine whether the amount of glue is
appropriate. The higher the density of the wood, the greater the
environmental humidity, and the lower the environmental
temperature, the longer the closing time.
4. Please complete the environment temperature above 25℃ within 5
minutes. The longer the aging time, the higher the viscosity of the
adhesive layer and the lower the permeability. The aging time after
cloth glue usually varies with the amount of cloth glue and the
temperature and humidity of the operating environment. The shorter
the aging time, the faster the pressure is applied, and the better
the bonding strength can be ensured.
5. After the pressure is relieved, the board should be kept for at
least 4 hours after the indoor temperature is above 25℃ before
entering the next process. After 7 days of curing, it will reach
the super good bonding strength.
6. Operation and use: This product contains isocyanate, so you
should wear protective gloves suitable for isocyanate. You should
wear goggles every time you use the product. The curing agent must
not come into contact with water or moisture.
7. Cleaning: It must be cleaned before the system is cured.
8. Glue-The cured glue can be treated as a general harmless waste.
Curing agent-contains isocyanate and should be treated as hazardous
waste.
The mixed glue and curing agent-after they are completely cured,
they can be treated as general harmless waste.