AirBag Label Application Flame Resistance Cross Laminated Film
Description:
Cross Laminated Film is an extremely versatile, high-performance product line that resists
tearing, puncturing, and weathering. Our proprietary, cross-lamination manufacturing
process provides considerably tighter gauge control than competitive spun bonded,
smoother printing surfaces, and ease in converting.
It is so strong that it will not tear, even when nicked, and withstands cold temperature.
UV stabilized, standard grades hold up well during outdoor exposure and provides
superior moisture and chemical resistance making it ideal for engine tags as well as
cruise and freight tags.
Parameter:
| NO. | Item | Performance | ||
| SDM-30 | SDM-60 | |||
| 1 | Tensile Property | Tensile Strength/Mpa ≥ | 30 | 50 |
| MaxF/(N/50mm) ≥ | 200 | 300 | ||
| Elongation as MaxF/% ≥ | 200 | |||
| Elongation at break/% ≥ | 250 | |||
| 2 | Sample number of no broken tested by free-falling dart method ≥ | 8 | ||
| 3 | Tear Strength(Nail Shank)/N ≥ | 60 | ||
| 4 | Angle Tear Strength/N ≥ | 25 | ||
| 5 | Thermal Stability | 120 ℃,10min, No bulb, No deformation | ||
| 6 | Cryogenic Flexibility ℃ | -35℃, No fissure, No delamination | ||
| 7 | Thermal Ageing | Appearance | No bulb, No deformation | |
| Subsequent MaxF/% ≥ | 80 | |||
| Elongation at MaxF/% ≥ | 200 | |||
| Elongation at break/% ≥ | 200 | |||
| 8 | Artificial Weathering | Appearance | No bulb, No deformation | |
| Subsequent MaxF/% ≥ | 70 | |||
| Elongation at MaxF/% ≥ | 180 | |||
| Elongation at break/% ≥ | 180 | |||
Advantages:
► Corona treated
► Outdoor Durability:
► Good ink adhesion
► Chemical and Oil Resistance
► Pre-printed or print-on-demand
► Excellent Staple Pullout Resistance
► Flame Resistance
Application: