Active Member
|
[China]
Address: Block. 7, Zone C, Auto Parts industrial Park, Tianyuan Dist., Zhuzhou, Hunan, China (Mainland)
Contact name:Shirley Pan
Zhuzhou Zhenfang Yaguang Tungsten Molybdenum Co., LTD. |
|
|
Dia6x62mm Ground Tungsten Carbide / Cobalt Rod for Diamond Cutting Tool
Products Details:
1. Size: Dia6x62mm other size also available
2. Material: Virgin Tungsten Carbide(WC+Co)
3. Grade: YG8/YL10.2
4. Hardness: HRA89/92
5. Surface: Polished
6. Tolerance: +0.05 based on requirement
7. Grain Size: 0.6-0.8μm
8. Propferties: good abrasive resistance
9. Application: diamond cutting tools parts
Introduction and Main application of tungsten carbide rod
Tungsten Carbide is a kind of Hard Metal due to it’s very high hardness compare to other metals. TypicallyTungsten Carbide can have a hardness value of 1600 HV, is 10 times of mild steel.
Tungsten Carbides is mainly used for making drills, endmills, reamers, etc. It have a wide range of application in many industry sectors such as metal machining, wear parts for mining and oil industries, metal forming tools, cutting tips for saw blades and have now expanded to include consumer items such as watch cases and wedding rings, plus the ball that is in many ball point pens.
Application Industries:
Paper, packaging, printing, Petroleum, Non-ferrous metal processing, Electronic,Mechanical, Chemical,, Metallurgy, Defense industries
Common Unground Dimension and Tolerance
| Dimension | Tolerance of diameter(mm) | Tolerance of length(mm) |
| ZF-Φ4.0×330 | +0.3/+0.5 | +0/+5.0 |
| ZF-Φ6.0×330 | ||
| ZF-Φ8.0×330 | ||
| ZF-Φ10.0×330 | ||
| ZF-Φ10.0×330 |
+0.30/+0.70
| +0/+5.0
|
| ZF-Φ12.0×330 | ||
| ZF-Φ14.0×330 | ||
| ZF-Φ16.0×330 | ||
| ZF-Φ18.0×330 |
+0.40/+1.0
| +0/+5.0
|
| ZF-Φ20.0×330 | ||
| ZF-Φ22.0×330 | ||
| ZF-Φ24.0×330 | ||
| ZF-Φ26.0×330 | ||
| ZF-Φ28.0×330 | ||
ZF-Φ30.0×330 | ||
| ZF-Φ32.0×330 | +0.7/+1.5 | +0/+5.0 |
| ZF-Φ34.0×330 | ||
| We are able to help you customized various diameter and length carbide rod. gound or unground both available | ||
The tungsten carbide rods we can offer as following:
Some grade information for Reference
| Grade | Density g/cm3 | Hardness HRA(hv) | T.R.S (M Pa) | Grain Size(μm) |
| YL10.2 | 14.5 | 92.5 | 3800 | 0.6-0.8 |
| YG6 | 14.9 | 89.5 | 2150 | 0.8-1.2 |
| YG8 | 14.6 | 89 | 2320 | 0.8-1.2 |
| YG11 | 14.4 | 87.5 | 2260 | 0.8-1.2 |
| YG15 | 14.1 | 86.5 | 2400 | 0.8-1.2 |
| YS2T | 14.45 | 92.5 | 2800 | 0.6-0.8 |
| YNi8 | 14.6 | 88.5 | 1710 | 0.8-1.2 |
Our advantage of tungsten carbide rod
* We have over ten year experience
* ISO 9001:2015 Certification
* Use 100% tungsten carbide raw material
* Advanced technology , automatic pressing , HIP sintering
* Strict inspection for quality of raw material and finished products
* And precision grinding
* the tolerance of polish and ground can be +0.005/-0.005mm
* Full ability to accept OEM & ODM orders
* Stringent quality control and quality consistency.
Manufacturing process of tugnsten carbide rod
Tungsten Carbide Hard Metals are primarily produced using a Powder Metallurgy process, whereby the powdered forms of tungsten carbide and cobalt are mixed using ball mills, a binder material is added to hold the powders together during the next stage of the process which is compaction or pressing.
During the compaction processes, hydraulic presses or isostatic presses are used to compact the powders into a shape which approximates the design of the finished product.
Whilst in this condition, the powder compact can be easily machined using conventional metal working tools. This process is often referred to as “Green Machining”. Care has to be taken with the removal of the fine powder particles as they can pose a health hazard so effective extraction methods are required.
Following “Green Machining” the powder compact is then ready to be Sintered. Typically this is done in a vacuum furnace at temperatures between 1300 and 1600°C.
The sintering process causes the tungsten carbide and cobalt matrix to fuse together to produce a dense “Hard Metal”.
After sintering the material is so hard that it can only be machined by diamond grinding, a specialised form of micro machining that is relatively expensive as it is not possible to remove large amounts of materials by this process.