ASTM Grade 2 3 5,Medical Dental Titanium Disc With ASTM F67 F136 For Crowns, Bridges, Abutments, Dental Prosthetics
| BaseTi - Dental Pure Titanium Disc Inventory | ||
| Grade | Stock Size | Weight(kg) |
| ASTM Grade 2 ASTM Grade 3 | Φ98mm*10mm | 0.34 |
| Φ98mm*12mm | 0.41 | |
| Φ98mm*14mm | 0.48 | |
| Φ98mm*16mm | 0.54 | |
| Φ98mm*18mm | 0.61 | |
| Φ98mm*20mm | 0.68 | |
| Φ98mm*22mm | 0.75 | |
| Φ98mm*24mm | 0.82 | |
| Φ98mm*25mm | 0.85 | |
| BaseTi - Dental Titanium Alloy Disc Inventory | ||
| Grade | Stock Size | Weight(kg) |
| ASTM Grade 5 Ti-6Al-4V | Φ98mm*10mm | 0.34 |
| Φ98mm*12mm | 0.41 | |
| Φ98mm*14mm | 0.48 | |
| Φ98mm*16mm | 0.54 | |
| Φ98mm*18mm | 0.61 | |
| Φ98mm*20mm | 0.68 | |
| Φ98mm*22mm | 0.75 | |
| Φ98mm*24mm | 0.82 | |
| Φ98mm*25mm | 0.85 | |
*The dimensions listed in the table above represent the sizes we regularly supply, and we have ample stock available. *Should you require customized dimensions for your titanium discs, or specific tolerance parameters, we are able to complete production within a swift timeframe of 10 to 15 days. | ||
The Ultimate Guide to Dental Titanium Discs:
Applications and Benefits Across Grades
When it comes to dental prosthetics and implants, the material
choice is paramount. Among the top choices in the industry are
dental titanium discs, which offer a combination of mechanical
strength, corrosion resistance, and biocompatibility.
Dental Titanium Discs: An Overview by BaseTi
Dental titanium discs are widely used for milling dental
prosthetics and implants. In the market, these discs generally fall
under three main ASTM grades: Grade 2, Grade 3, and Grade 5.
Applications Across Grades
Material: Pure Titanium
Applications: Crowns, bridges, and less-load-bearing implants.
Advantage: Exceptional biocompatibility and corrosion resistance.
Material: Pure Titanium, slightly more alloyed than Grade 2.
Applications: Implants and abutments.
Advantage: Higher mechanical strength compared to Grade 2.
Material: Titanium alloyed with Aluminum and Vanadium.
Applications: High-load-bearing implants and complex dental
prosthetics.
Advantage: Highest mechanical strength among all grades.
Product Case Studies
Pure Titanium Dental Discs for Dental Crowns
A dental practice opted for Grade 2 titanium discs to create dental
crowns. The success rate and patient satisfaction were
overwhelmingly high due to the disc's superior biocompatibility.
Dental Implant Disc in Complex Cases
In a recent application, Grade 5 titanium discs from BaseTi were
used to mill dental implants for patients requiring high
load-bearing capacity. The results were favorable, showcasing
excellent strength and long-term durability.
Why Choose Titanium?
As a leading titanium manufacturer and supplier, BaseTi offers a
range of titanium products that comply with the highest quality
standards. We provide dental titanium discs with exceptional
tolerances, ideal for applications requiring precision and
reliability.
Titanium Dental Milling Disc Versus Others
Titanium offers a balance of mechanical strength and
biocompatibility that's hard to find in other materials. Its
adaptability to computer-aided design and manufacturing (CAD/CAM)
technologies makes it a go-to material in dental milling
applications.
Conclusion
With the variety of grades available, dental titanium discs are set
to remain a cornerstone in dental prosthetics and implants. For any
questions about product selection, don't hesitate to consult
BaseTi, a trusted titanium factory and supplier.
Production Standards: ASTM F67 (USA), EN ISO 5832-2 (Europe)
Application Field: Dental crowns, dental implants
Ti Disc Tolerance: +/- 0.1 mm
Biocompatibility: High
Mechanical Strength: Moderate
Corrosion Resistance: Excellent
Surface Finish: Smooth, Ra<0.5μm
Diameter and Thickness: 98mm x 12-25mm
Milling Compatibility: Good
Sterilizability: Excellent
Production Standards: ASTM F67 (USA), EN ISO 5832-2 (Europe)
Application Field: Dental implants, abutments
Ti Disc Tolerance: +/- 0.1 mm
Biocompatibility: High
Mechanical Strength: Moderate-High
Corrosion Resistance: Excellent
Surface Finish: Smooth, Ra<0.5μm
Diameter and Thickness: 98mm x 12-25mm
Milling Compatibility: Good
Sterilizability: Excellent
Production Standards: ASTM F136 (USA), EN ISO 5832-3 (Europe)
Application Field: Dental prosthetics, dental implants
Ti Disc Tolerance: +/- 0.1 mm
Biocompatibility: High
Mechanical Strength: High
Corrosion Resistance: Excellent
Surface Finish: Smooth, Ra<0.5μm
Diameter and Thickness: 98mm x 12-25mm
Milling Compatibility: Good
Sterilizability: Excellent
Attribute | ASTM Grade 2 | ASTM Grade 3 | ASTM Grade 5 |
|---|---|---|---|
U.S. Standards | ASTM F67 | ASTM F67 | ASTM F136 |
European Standards | EN ISO 5832-2 | EN ISO 5832-2 | EN ISO 5832-3 |
Material | Pure Titanium | Pure Titanium (more alloyed than Grade 2) | Titanium Alloy (Ti6Al4V) |
Applications | Dental crowns, bridges | Dental implants, abutments | High-load-bearing implants, complex dental prosthetics |
Specific Products | Dental Crowns and Bridges, Less-load-bearing dental implants | Dental Implants and Abutments, more load-bearing compared to Grade 2 | Complex Dental Prosthetics, High-load-bearing dental implants |
The physical properties of dental titanium discs vary depending on the grade of the material and the respective standards they meet. Below is a comprehensive table that encapsulates these vital features:
| Attribute | ASTM F67 (U.S.) | ASTM F136 (U.S.) | EN ISO 5832-2 (EU) | EN ISO 5832-3 (EU) |
|---|---|---|---|---|
| Grade | Grade 2 | Grade 5 | Grade 2 | Grade 5 |
| Density (g/cm³) | 4.51 | 4.43 | 4.51 | 4.43 |
| Tensile Strength (MPa) | 345-450 | 930-1030 | 345-450 | 930-1030 |
| Yield Strength (MPa) | 275-450 | 860-880 | 275-450 | 860-880 |
| Elongation (%) | 20 | 10-16 | 20 | 10-16 |
| Hardness (HV) | 120-180 | 350-440 | 120-180 | 350-440 |
Element | ASTM F67 Grade 2 (%) | ASTM F136 Grade 5 (%) | EN ISO 5832-2 Grade 2 (%) | EN ISO 5832-3 Grade 5 (%) |
|---|---|---|---|---|
C | ≤ 0.10 | ≤ 0.08 | ≤ 0.10 | ≤ 0.08 |
O | ≤ 0.25 | ≤ 0.20 | ≤ 0.25 | ≤ 0.20 |
N | ≤ 0.03 | ≤ 0.05 | ≤ 0.03 | ≤ 0.05 |
H | ≤ 0.015 | ≤ 0.012 | ≤ 0.015 | ≤ 0.012 |
Fe | ≤ 0.30 | ≤ 0.25 | ≤ 0.30 | ≤ 0.25 |
Al | -- | 5.5-6.75 | -- | 5.5-6.75 |
V | -- | 3.5-4.5 | -- | 3.5-4.5 |