Inventory ASTM Grade 2, Grade 3, CP Titanium Disc Dental, Grade 5 Dental Titanium Alloy Disc, ASTM F136, ASTM F67
| BaseTi - Dental Pure Titanium Disc Inventory | ||
| Grade | Stock Size | Weight(kg) |
| ASTM Grade 2 ASTM Grade 3 | Φ98mm*10mm | 0.34 |
| Φ98mm*12mm | 0.41 | |
| Φ98mm*14mm | 0.48 | |
| Φ98mm*16mm | 0.54 | |
| Φ98mm*18mm | 0.61 | |
| Φ98mm*20mm | 0.68 | |
| Φ98mm*22mm | 0.75 | |
| Φ98mm*24mm | 0.82 | |
| Φ98mm*25mm | 0.85 | |
| BaseTi - Dental Titanium Alloy Disc Inventory | ||
| Grade | Stock Size | Weight(kg) |
| ASTM Grade 5 Ti-6Al-4V | Φ98mm*10mm | 0.34 |
| Φ98mm*12mm | 0.41 | |
| Φ98mm*14mm | 0.48 | |
| Φ98mm*16mm | 0.54 | |
| Φ98mm*18mm | 0.61 | |
| Φ98mm*20mm | 0.68 | |
| Φ98mm*22mm | 0.75 | |
| Φ98mm*24mm | 0.82 | |
| Φ98mm*25mm | 0.85 | |
*The dimensions listed in the table above represent the sizes we regularly supply, and we have ample stock available. *Should you require customized dimensions for your titanium discs, or specific tolerance parameters, we are able to complete production within a swift timeframe of 10 to 15 days. | ||
Dental Titanium Discs: Your Comprehensive Guide to Grades and
Applications
In the dental industry, material selection can make or break the
final product. Among the preferred materials are Dental Titanium
Discs, renowned for their biocompatibility and mechanical
robustness. This article aims to guide overseas buyers through the
maze of titanium grades and their applications in the dental
industry.
Choosing the right grade is essential for meeting the rigorous standards of dental applications. In the U.S., ASTM F67 and ASTM F136 standards govern these materials, while in Europe, EN ISO 5832-2 and EN ISO 5832-3 are followed.
ASTM Grade 2 (Pure Titanium Dental Disc)
Composition: Pure Titanium
Standard: ASTM F67, EN ISO 5832-2
Applications: Dental crowns, bridges
Supplier: BaseTi
ASTM Grade 3
Composition: Pure Titanium with enhanced tensile strength
Standard: ASTM F67, EN ISO 5832-2
Applications: Implant abutments, frameworks
ASTM Grade 5 (Ti Dental Milling Disc)
Composition: Titanium Alloy (Ti6Al4V)
Standard: ASTM F136, EN ISO 5832-3
Applications: High-load implants, orthodontic devices
Supplier: BaseTi
Let's delve into specific applications within the dental field:
Dental Crowns and Bridges (ASTM Grade 2)
Pure Titanium Dental Discs under ASTM Grade 2 supplied by BaseTi
are ideal for crafting dental crowns and bridges. These discs offer
superior corrosion resistance and are easy to mill.
Implant Abutments (ASTM Grade 3)
ASTM Grade 3 is perfect for implant abutments, offering higher
mechanical strength while still maintaining excellent
biocompatibility.
High-Load Implants and Orthodontic Devices (ASTM Grade 5)
BaseTi's Titanium Dental Milling Discs in ASTM Grade 5 are designed
for high-load implants and advanced orthodontic devices. The
Ti6Al4V alloy provides unmatched strength and durability.
As a leading titanium factory and titanium manufacturer, BaseTi provides top-notch Dental Titanium Alloy Discs and Dental Implant Discs. With a variety of grades available, we are your go-to titanium supplier for all your dental application needs.
Understanding the right grade and corresponding application of
Dental Titanium Discs is crucial. Whether you are dealing with
crowns, bridges, or advanced orthodontic devices, the appropriate
grade selection could be your key to success.
Attribute | ASTM Grade 2 | ASTM Grade 3 | ASTM Grade 5 |
|---|---|---|---|
U.S. Standards | ASTM F67 | ASTM F67 | ASTM F136 |
European Standards | EN ISO 5832-2 | EN ISO 5832-2 | EN ISO 5832-3 |
Material | Pure Titanium | Pure Titanium (more alloyed than Grade 2) | Titanium Alloy (Ti6Al4V) |
Applications | Dental crowns, bridges | Dental implants, abutments | High-load-bearing implants, complex dental prosthetics |
Specific Products | Dental Crowns and Bridges, Less-load-bearing dental implants | Dental Implants and Abutments, more load-bearing compared to Grade 2 | Complex Dental Prosthetics, High-load-bearing dental implants |
The physical properties of dental titanium discs vary depending on the grade of the material and the respective standards they meet. Below is a comprehensive table that encapsulates these vital features:
| Attribute | ASTM F67 (U.S.) | ASTM F136 (U.S.) | EN ISO 5832-2 (EU) | EN ISO 5832-3 (EU) |
|---|---|---|---|---|
| Grade | Grade 2 | Grade 5 | Grade 2 | Grade 5 |
| Density (g/cm³) | 4.51 | 4.43 | 4.51 | 4.43 |
| Tensile Strength (MPa) | 345-450 | 930-1030 | 345-450 | 930-1030 |
| Yield Strength (MPa) | 275-450 | 860-880 | 275-450 | 860-880 |
| Elongation (%) | 20 | 10-16 | 20 | 10-16 |
| Hardness (HV) | 120-180 | 350-440 | 120-180 | 350-440 |
Element | ASTM F67Grade 2 (%) | ASTM F136 Grade 5 (%) | EN ISO 5832-2 Grade 2 (%) | EN ISO 5832-3 Grade 5 (%) |
|---|---|---|---|---|
C | ≤ 0.10 | ≤ 0.08 | ≤ 0.10 | ≤ 0.08 |
O | ≤ 0.25 | ≤ 0.20 | ≤ 0.25 | ≤ 0.20 |
N | ≤ 0.03 | ≤ 0.05 | ≤ 0.03 | ≤ 0.05 |
H | ≤ 0.015 | ≤ 0.012 | ≤ 0.015 | ≤ 0.012 |
Fe | ≤ 0.30 | ≤ 0.25 | ≤ 0.30 | ≤ 0.25 |
Al | -- | 5.5-6.75 | -- | 5.5-6.75 |
V | -- | 3.5-4.5 | -- | 3.5-4.5 |