Before the appearing of PA66 thermal break strips, the most commonly used is PVC insulation strips. After foreign advanced ideas were brought into China, PA66 strips appeared. PVC strips are cheap, so there is a large market, but its thermal insulation contribution is negligible, even seriously affect the overall quality of the windows and doors, it is impossible to play the role of energy conservation and environmental protection. Therefore, with better living colnditions, polyamide 66 reinforced by 25% glass fiber thermal break strips are being widespreadly used in our daily decoration. they are inserted into aluminum window, door and facade profile for thermal insulation.
The shape I thermal barrier polyamide strip can prevent the window
frame from dust and water, has a better mechanical performance, is
the first generation and easiest shape of insulating strips.
For the shape I, we can provide the following size or customize according to customers’ requirements.
high quality, competitive price, free sample support and short lead time, high mechanical strength, high toughness, high softening point, good wear resistance, self-lubrication, long-term work at higher temperatures, high CTI value, excellent electrical insulation, low smoke and toxicity characteristics.
It is mainly used in insulation broken bridge aluminium products, helping to reduce heat loss or heat gain through the aluminum, and has better performance in terms of power usage.
Item | Unit | GB/T 23615.1-2009 | BY-Technical specification |
Density | g/cm3 | 1.3±0.05 | 1.28-1.35 |
Linear expansion coefficient | K-1 | (2.3-3.5)×10-5 | (2.3-3.5)×10-5 |
Vicat softening temperature | ºC | ≥230ºC | ≥233ºC |
Melting point | ºC | ≥240 | ≥240 |
Testing for tensile cracks | - | No cracks | No cracks |
Shore hardness | - | 80±5 | 80-85 |
Impact strength(Unnotched) | KJ/m2 | ≥35 | ≥38 |
Tensile strength(longitudinal) | MPa | ≥80a | ≥82a |
Elasticity modulus | MPa | ≥4500 | ≥4550 |
Elongation at break | % | ≥2.5 | ≥2.6 |
Tensile strength(transverse) | MPa | ≥70a | ≥70a |
High temperature tensile strength(transverse) | MPa | ≥45a | ≥47a |
Low temperature tensile strength(transverse) | MPa | ≥80a | ≥81a |
Water resistance tensile strength(transverse) | MPa | ≥35a | ≥35a |
Aging resistance tensile strength(transverse) | MPa | ≥50a | ≥50a |