Product Description:
Glass fiber reinforced PA 6.6 granules with heat aging resistance extrusion moulding grade. It's good raw material for thermal break profiles of high stiffness and dimensional stability.
PA66GF25 granules are based on PA66 resin. Then the granules are formed by twin-screw extrusion machine after adding fiberglass, efficient flame retardants and various additives.
Why use PA as raw material:
PA has the advantages of high mechanical strength, high softening point, good wear resistance, self-lubrication, cushioning, sound deadening, excellent oil and chemical corrosion resistance, and good electrical insulation. Because of these superior performance, PA composite have already replaced some metals being as structural materials.
Polywell PA66 Granules Performance Table
NO. | Item | Unit | GB/T 23615.1-2009 | PW-Technical specification |
|---|---|---|---|---|
| Material Properties | |||
1 | Density | g/cm3 | 1.3±0.05 | 1.28-1.35 |
2 | Linear expansion coefficient | K-1 | (2.3-3.5)×10-5 | (2.3-3.5)×10-5 |
3 | Vicat softening temperature | ºC | ≥230ºC | ≥233ºC |
4 | Melting point | ºC | ≥240 | ≥240 |
5 | Testing for tensile cracks | - | No cracks | No cracks |
6 | Shore hardness | - | 80±5 | 80-85 |
7 | Impact strength(Unnotched) | KJ/m2 | ≥35 | ≥38 |
8 | Tensile strength(longitudinal) | MPa | ≥80a | ≥82a |
9 | Elasticity modulus | MPa | ≥4500 | ≥4550 |
10 | Elongation at break | % | ≥2.5 | ≥2.6 |
11 | Tensile strength(transverse) | MPa | ≥70a | ≥70a |
12 | High temperature tensile strength(transverse) | MPa | ≥45a | ≥47a |
13 | Low temperature tensile strength(transverse) | MPa | ≥80a | ≥81a |
14 | Water resistance tensile strength(transverse) | MPa | ≥35a | ≥35a |
15 | Aging resistance tensile strength(transverse) | MPa | ≥50a | ≥50a |
1.Sample water content less than 0.2% by weight.
2.Norm laboratory condition:(23±2)ºC and (50±10)% relative
humidity.
3.The specifications marked with "a" only applies to I-shape strip
otherwise, the specifications concluded between supplier and buyer
through consultation, shall be written in contract or purchase
order.
Advantages of our PA6.6-gf25 granules:
Our company has devoted more than ten years to the research and development and production of nylon extruding profiles. According to customer reaction, using our PA66 granules for production can get high yield, easy start-up, and get less scrap in the early start-up stage. There will be no lack or incomplete of profiles in the production process, thus avoiding material waste, saving customer costs and improving production efficiency.
Application:
The PA66 granules with fiber glass are mainly used in thermal break strips, which are used in aluminum windows and doors.
Packaging:
Pack in woven bags. Each bag is 25 kg.
Lead time:
10-15 working days after receiving the deposit.
FAQ:
Q: About Sample
A: Sample is Free, but the express fee is collect or you pay us the cost in advance.
Q: About MOQ
A: For the polyamide granules, MOQ is 1 ton. For the thermal break strips, MOQ is 5,000 meters.
Q: About Customizing Package Style and Marks
A: You can customize the package style and marks.
Q: About warranty
A: We are confident in our products, and pack them well before delivery, so usually you will receive your order in good condition. Any quality issue, we will deal with it immediately.
Q: About Payment or other question
A: 50% T/T deposit before production, 50% T/T balance before loading.
For any other questions, please feel free to contact:
Camille
E-mail:camille@szpolywell.cn
Phone:0086-13584481777 (WhatsApp)
Wechat:Camille_4790
Address: Zhangjiagang City, Jiangsu Province, China