Product Introduction:
Polyamide 6.6 granules reinforced by fiberglass, with special additives, is blended and extruded by twin screw extrusion machine. It is more suitable for extrusion of heat insulation strip. Compared with ordinary granules, it is more conducive to forming. It has certain advantages in speed, surface finish and yield. The performances of nylon insulating strip produced made of this material meet the national standards. It can not only be customized according to customer requirements, far exceeding the national standard, but also can add high-efficiency flame retardant to achieve the purpose of flame retardant.
Advantage:
1. Competitive price, free samples, short delivery period.
2. Low smoke and other characteristics.
3. Good wear resistance,self-lubrication,long-term work at high
temperature.
4. High CTI value,excellent electrical insulation.
5. Fast crystallization,fast forming,high temperature resistance.
6. Anti-ultraviolet radiation,anti-chemical agent corrosion.
7. High yield,easy start-up,and get less scrap in the early
start-up stage.
8. No lack or incomplete of profiles in the production process.
9. There are different formulations for different shapes.
Details of related standard:
Polywell PA66 Granules Performance Table
| NO. | Item | Unit | GB/T 23615.1-2009 | PW-Technical specification |
| Material Properties | ||||
| 1 | Density | g/cm3 | 1.3±0.05 | 1.28-1.35 |
| 2 | Linear expansion coefficient | K-1 | (2.3-3.5)*10-5 | (2.3-3.5)*10-5 |
| 3 | Vicat softening temperature | ºC | ≥230ºC | ≥233ºC |
| 4 | Melting point | ºC | ≥240 | ≥240 |
| 5 | Testing for tensile cracks | - | No cracks | No cracks |
| 6 | Shore hardness | - | 80±5 | 80-85 |
| 7 | Impact strength(Unnotched) | KJ/m2 | ≥35 | ≥38 |
| 8 | Tensile strength(longitudinal) | MPa | ≥80a | ≥82a |
| 9 | Elasticity modulus | MPa | ≥4500 | ≥4550 |
| 10 | Elongation at break | % | ≥2.5 | ≥2.6 |
| 11 | Tensile strength(transverse) | MPa | ≥70a | ≥70a |
| 12 | High temperature tensile strength(transverse) | MPa | ≥45a | ≥47a |
| 13 | Low temperature tensile strength(transverse) | MPa | ≥80a | ≥81a |
| 14 | Water resistance tensile strength(transverse) | MPa | ≥35a | ≥35a |
| 15 | Aging resistance tensile strength(transverse) | MPa | ≥50a | ≥50a |
1. Sample water content less than 0.2% by weight.
2. Norm laboratory condition:(23±2)ºC and (50±10)% relative
humidity.
3. The specifications marked with "a" only applies to I-shape strip
otherwise, the specifications concluded between supplier and buyer
through consultation, shall be written in contract or purchase
order.
Our Company
Suzhou Polywell Engineering Plastics Company is located in the city of Zhangjiagang, Jiangsu Province, China. Our company has devoted more than ten years to the research and development and production of nylon extruding profiles. According to customer reaction, using our PA66 granules for production can get high yiedl, easy start-up, and get less scrap in the early start-up stage. There will be no lack or incomplete of profiles in the production process, thus avoiding material waste.
Application:
The PA66 granules with fiber glass are mainly used in thermal break
strips, which are used in aluminum windows and doors. Our granules
have good fluidity thus guaranteeing your smooth production. The good raw material can reduce the rate of
rejects, and can produce high quality strips.
Packaging & Delivery:
Packaging details:25kg/bag
Delivery details: shipped in 5-10 working days after receiving the payment